Abstract:Ni-rich cathode material is one of the most promising materials for Li-ion batteries in electric vehicles. However, fading capacity, poor cyclic stability and high pH value are still major challenges, which suppress its practical application. In this study, spherical LiNi0.9Co0.08Al0.02O2 powders with 0.4 wt% TiO2 coating layer were prepared by impregnation–hydrolysis method. Scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD) results show that TiO2 is uniformly coated on the surface of LiNi0.9Co0.08Al0.02O2 particle and slightly embedded into LiNi0.9Co0.08Al0.02O2 particles. After 100 cycles at 2.0C, 0.4 wt% TiO2-coated LiNi0.9Co0.08Al0.02O2 electrode delivers much higher discharge capacity retention (77.0%) than the pristine LiNi0.9Co0.08Al0.02O2 electrode (63.3%). The excellent cycling performance of 0.4 wt% TiO2-coated LiNi0.9Co0.08Al0.02O2 electrode at a high discharge ratio is due to a TiO2 coating layer which can effectively reduce the direct contact between cathode material and electrolyte, suppress the oxidation of electrolyte, improve electrical conductivity of the electrode and increase the stability of the structure.<h3 class="a-plus-plus">Graphic abstract</h3> With the increase of current density, TCNC sample clearly exhibits enhanced cycling performance with higher capacity retention, and the capacity retention of TCNC increases by 22% at 2.0 C.

Enabling Enhanced Cycling Stability of a LiNi0.8Co0.15Al0.05O2 Cathode by Constructing a Ti-Rich Surface

Enhanced Electrochemical Performance of LiNi0.8Co0.15Al0.05O2 Cathode Material via Li2TiO3 Nanoparticles Coating

Realizing Superior Cycling Stability of Ni-Rich Layered Cathode by Combination of Grain Boundary Engineering and Surface Coating

Stabilizing high-Ni cathodes with gradient surface Ti-enrichment

Cycling stability of LiNi0.80Co0.15Al0.05O2 cathode modified by solid-state electrolyte film

Enhancing the Structural Stability and Electrochemical Performance of High-Nickel Cathode Materials through Ti Doping with an Exothermic Non-oxide Precursor

Surface Coating with Li-Ti-O to Improve the Electrochemical Performance of Ni-rich Cathode Material

Improved Cycling Stability of Ni-Rich Cathode Material by In Situ Introduced TM-B-O Amorphous Surface Structure

Improved cycling stability of high nickel cathode material for lithium ion battery through Al- and Ti-based dual modification

Enabling stable and high-rate cycling of a Ni-rich layered oxide cathode for lithium-ion batteries by modification with an artificial Li<SUP>+</SUP>-conducting cathode-electrolyte interphase

The cycle performance of high nickel cathode materials significantly enhanced by the LiAlO2@Al2O3 dual-modified coating

Boosting cyclability performance of the LiNi0.8Co0.15Al0.05O2 cathode by a polyacrylonitrile-induced conductive carbon surface coating

Optimized structure stability and cycling performance of LiNi0.8Co0.1Mn0.1O2 through homogeneous nano-thickness Al2O3 coating

Improving the Performance of LiNi0.925Co0.065Mn0.01O2 via Ti4+& Nb5+ Co-Modifications

(Digital Presentation) Simultaneous Transforming Residual Lithium Compounds and Stabilizing Surface Lattice Oxygen for Ni-Rich Cathode Via Atomic Layer Deposition and Post-Annealing

Conversion of residual lithium into fast ionic conductor coating to achieve one-step double modification strategy in LiNi0.8Co0.15Al0.05O2

Surface Encapsulation of Layered Oxide Cathode Material with NiTiO 3 for Enhanced Cycling Stability of Na-Ion Batteries

Surface enrichment and diffusion enabling gradient-doping and coating of Ni-rich cathode toward Li-ion batteries

Anchoring Interfacial Nickel Cations by Tunable Coordinative Structure for Highly Stabilized Nickel-Rich Layered Oxide Cathodes

Constructing Stable Interface Layer for Boosting High-Voltage Cycling Performance of Single-Crystal Ni-rich Cathodes

TiO2-coated LiNi0.9Co0.08Al0.02O2 cathode materials with enhanced cycle performance for Li-ion batteries