TiO2-coated LiNi0.9Co0.08Al0.02O2 cathode materials with enhanced cycle performance for Li-ion batteries

Wei-Wei Li,Xiang-Jun Zhang,Jiang-Ju Si,Jie Yang,Xue-Yi Sun

DOI: https://doi.org/10.1007/s12598-020-01483-5

IF: 6.318

2020-07-04

Rare Metals

Abstract:<span class="a-plus-plus abstract-section id-a-sec1"><p class="a-plus-plus">Ni-rich cathode material is one of the most promising materials for Li-ion batteries in electric vehicles. However, fading capacity, poor cyclic stability and high pH value are still major challenges, which suppress its practical application. In this study, spherical LiNi<sub class="a-plus-plus">0.9</sub>Co<sub class="a-plus-plus">0.08</sub>Al<sub class="a-plus-plus">0.02</sub>O<sub class="a-plus-plus">2</sub> powders with 0.4 wt% TiO<sub class="a-plus-plus">2</sub> coating layer were prepared by impregnation–hydrolysis method. Scanning electron microscopy (SEM), high-resolution transmission electron microscopy (HRTEM) and X-ray diffraction (XRD) results show that TiO<sub class="a-plus-plus">2</sub> is uniformly coated on the surface of LiNi<sub class="a-plus-plus">0.9</sub>Co<sub class="a-plus-plus">0.08</sub>Al<sub class="a-plus-plus">0.02</sub>O<sub class="a-plus-plus">2</sub> particle and slightly embedded into LiNi<sub class="a-plus-plus">0.9</sub>Co<sub class="a-plus-plus">0.08</sub>Al<sub class="a-plus-plus">0.02</sub>O<sub class="a-plus-plus">2</sub> particles. After 100 cycles at 2.0C, 0.4 wt% TiO<sub class="a-plus-plus">2</sub>-coated LiNi<sub class="a-plus-plus">0.9</sub>Co<sub class="a-plus-plus">0.08</sub>Al<sub class="a-plus-plus">0.02</sub>O<sub class="a-plus-plus">2</sub> electrode delivers much higher discharge capacity retention (77.0%) than the pristine LiNi<sub class="a-plus-plus">0.9</sub>Co<sub class="a-plus-plus">0.08</sub>Al<sub class="a-plus-plus">0.02</sub>O<sub class="a-plus-plus">2</sub> electrode (63.3%). The excellent cycling performance of 0.4 wt% TiO<sub class="a-plus-plus">2</sub>-coated LiNi<sub class="a-plus-plus">0.9</sub>Co<sub class="a-plus-plus">0.08</sub>Al<sub class="a-plus-plus">0.02</sub>O<sub class="a-plus-plus">2</sub> electrode at a high discharge ratio is due to a TiO<sub class="a-plus-plus">2</sub> coating layer which can effectively reduce the direct contact between cathode material and electrolyte, suppress the oxidation of electrolyte, improve electrical conductivity of the electrode and increase the stability of the structure.</p></span><span class="a-plus-plus abstract-section id-a-sec2 outputmedium-online"><h3 class="a-plus-plus">Graphic abstract</h3><p class="a-plus-plus"> With the increase of current density, TCNC sample clearly exhibits enhanced cycling performance with higher capacity retention, and the capacity retention of TCNC increases by 22% at 2.0 C.</p></span>

materials science, multidisciplinary,metallurgy & metallurgical engineering