Abstract:The microstructure evolution of Mg-3Sn, Mg-3Sn-3Al-Zn (ATZ331), and Mg-3Sn-6Al-Zn (ATZ631) alloys during high-speed rolling (HSR) and annealing was studied. High-speed rolling was carried out on the three alloys at a rolling speed of 1100 m/min, a rolling temperature of 400 °C, and a reduction of 40% during a single pass. The results showed that the microstructure of the samples after HSR contained many twins and was dominated by {10−12} extension twins (ETs) and supplemented by {10−11} contraction twins (CTs) and {10−11}-{10−12} double twins (DTs). After adding Al, the content of these different types of twins was reduced. The twinning fraction decreased significantly with 3 wt% Al addition, while the twinning fraction decreased slightly with 6 wt% Al addition. The high-speed rolled alloys were annealed at 370 °C for 1 min, 2 min, 3 min, 5 min, and 8 min. When the annealing time was 1 min, the recrystallization fraction of the ATZ631 alloy was low, indicating that increasing the Al content to 6 wt% inhibited recrystallization. When the annealing time increased to 3 min, the recrystallized grains in the ATZ631 alloy grew, indicating that the grain growth progressed faster in this alloy. When the annealing time was 8 min, the grain size of the three alloys grew. The electron backscattered diffraction (EBSD) results of the alloy annealed for 8 min showed that the twin fraction in the annealed state was lower than that after high-speed rolling. In addition with the increase in Al content, the twin fraction decreased. During high-speed rolling, the maximum intensity also increased with an increase in Al content, were 22.72, 25.09, and 26.35, and the texture of the annealed alloy was weakened. The Al addition also increased the maximum intensity.

Annealing Behavior of 6061 Al Alloy Subjected to Differential Speed Rolling Deformation

Annealing Behavior of Nanostructured Aluminum Produced by Cold Rolling to Ultrahigh Strains

Effects Of Rolling Process On Microstructure And Mechanical Property Of 7050 Aluminum Alloy

Influence of alloy chemistry on the deformation behaviour and anisotropic properties of aluminium ultra-fine-grained thin sheets

Effects of annealing treatment on mechanical properties of 8011 aluminum alloy after cryogenic rolling

Thermal Stability of Aluminum Cold Rolled to Large Strain

Annealing Effect of High-Density Pulsed Electric Current Treatment on Cold-Rolled 6061 Aluminum Alloy

Microstructure evolution and recrystallization of Ti6246 alloy in hot‐rolling and annealing processes

Effect of Annealing on the Microstructure, Texture, and Properties of Cold-Rolled Ti50Ni47Fe3 Shape Memory Alloy Sheets

Influence of different rolling processes on the microstructures and mechanical properties of 6016 aluminum alloy

Effects of heat treatment on a novel continuous casting direct rolling 6056 aluminum alloy: cold rolling characteristics and tensile fracture properties

Controlled Annealing of Sandwich-Structured Aluminum AA1050 for Optimized Combinations of Strength and Ductility

Effect of Annealing Process on Microstructure and Properties of Rolled Semi-solid Billet

Microstructure and Microhardness Evolution of Mg-8Al-1Zn Magnesium Alloy Processed by Differential Speed Rolling at Elevated Temperatures

Mechanical property enhancement and microstructure evolution of an Al-Cu-Li alloy via rolling at different temperatures

Effect of Heat Treatment on the Microstructure and Properties of High Strain Rate Rolled 7050 Aluminum Alloy

Microstructure and Properties Evolution of 7075 Al alloy in Hot Rolling and Short Process Heat Treatment

Effect of Al addition and annealing on the microstructure evolution of Mg-3Sn Mg alloy subjected to high-speed rolling

The Effects of Rolling Deformation and Annealing Treatment on Damping Capacity of 1200 Aluminium Alloy

Aging behavior of Haynes 282 wrought nickel superalloy subjected to a cold pre-deformation by differential speed rolling

Effect of Annealing Time on Grain Structure Evolution and Superplastic Response of Al-Mg 5xxx Alloys