Abstract:Thin gauge nitrided grain-oriented silicon steel of 0.20 mm thickness and below shows pronounced surface effect during high temperature annealing. It is more prone to have anomalous microstructure and texture, leading to the decline of magnetic properties and its production is more difficult. Therefore, it is very important to find out the causes for the fluctuation in microstructure, texture, inhibitor state and magnetic properties so as to stabilize the product and reduce the production cost. In this paper, several samples showing different secondary recrystallization behaviors in production line are selected. The causes of different magnetic properties anomalies and the anomalous changes in texture were evaluated by means of a full high temperature annealing, the interrupted extraction test during secondary recrystallization and the determination of microstructure and texture of samples at each corresponding stage. The results show that the better magnetic properties correspond to the relatively high onset temperature of secondary recrystallization (1050 °C), larger primary grain size, strong primary recrystallization texture, thus forming a sharper Goss texture. The complete secondary recrystallization but poor magnetic properties correspond to the low onset temperature of secondary recrystallization (1020 °C), which is caused by the dual effects of the weak pinning of inhibitor and the smaller primary grain size leading to decrease in Goss texture sharpness. The reason of failed secondary recrystallization is attributed to the excessive pinning force of inhibitors, leading to the delayed onset temperature of secondary recrystallization or full fine-grained structure. In addition, low cold rolling reduction leads to low primary recrystallization texture intensity and the large number of {210} grains. However, the tendency of easy secondary recrystallization at low rolling reduction is suppressed by stronger inhibitor pinning and surface effect. The relationship between these anomalous phenomena and Als content, nitriding content, rolling reduction, primary recrystallization structure and texture was discussed.

The Relationship Between Hot and Cold Rolling Parameters and Secondary Recrystallization Behavior in Silicon Steel Sheets

Effect of heating rate of final annealing stage on secondary recrystallization in grain-oriented silicon steel

Effect of Secondary Cold Rolling Reduction Rate on Secondary Recrystallization Behavior of CGO Steel

Roles of Silicon Content and Normalization Temperature on Cold Workability and Recrystallization of High-Grade Non-Oriented Silicon Steel

Phenomenon and Cause Analysis of Different Secondary Recrystallization Behaviors in Thin-Gauge Grain-Oriented Silicon Steels

Influence Mechanisms of Cold Rolling Reduction Rate on Microstructure, Texture and Magnetic Properties of Non-Oriented Silicon Steel

Effects of Continuous Rolling and Reversible Rolling on 2.4% Si Non-Oriented Silicon Steel

Coordinate regulation mechanism of primary recrystallization texture and microstructure of grain-oriented silicon steel

Effect of Cold Rolling Process on Microstructure, Texture and Properties of Strip Cast Fe-2.6%Si Steel

Microstructural evolution and magnetic properties in strip cast non-oriented silicon steel produced by warm rolling

Effect of Double Cold Rolling on Magnetic Property and Microstructure of Non-Oriented High Silicon Steel Sheets Cast by Strip Casting Process

Recrystallization Behavior and Mechanical Properties of Az31b Alloy During the Hot-Rolling Process

Ultra‐Thin 3.5%Si Steel with Both Magnetic Properties and Mechanical Properties Produced by Different Process Routes of Large‐Scale Production

Effect of Grain Size Before Cold Rolling on Microstructure, Texture and Magnetic Properties of Ultra-Thin Low-Si Non-oriented Silicon Steel

Effect of recrystallization annealing temperature on microstructure, texture and magnetic properties of non-oriented silicon steel produced by strip casting

Investigation of microstructure and texture as related to primary recrystallization of grain-oriented silicon steel

Investigation on Recrystallization Behavior of Cold‐Rolled Silicon Steel in Continuous Heating with Three‐Point Bending Testing

Twin Roll Casting and Secondary Cooling of 6.0 wt.% Silicon Steel

Recrystallization and grain growth in hot rolling

Prediction and analysis of rolling process temperature field for silicon steel in tandem cold rolling

Dependence of recrystallization behavior and magnetic properties on grain size prior to cold rolling in high silicon non-oriented electrical steel