Dependence of recrystallization behavior and magnetic properties on grain size prior to cold rolling in high silicon non-oriented electrical steel

Zhi-Hong Li,Song-Kang Xie,Guo-Dong Wang,Hai-Tao Liu

DOI: https://doi.org/10.1016/j.jallcom.2021.161576

IF: 6.2

2021-12-01

Journal of Alloys and Compounds

Abstract:The present work aimed to investigate the roles of prior grain size of the hot rolled sheets after normalization on final recrystallization behavior and magnetic properties in 3.1%Si + 0.9%Al non-oriented electrical steel. Bigger prior grain size produced coarser deformed grains and promoted the development of in-grain shear bands, which together resulted in distinct recrystallization behavior. The prior small-grained microstructure caused relatively slow kinetics at the early stage of recrystallization, while fast kinetics was displayed at the later stage due to the growth of new γ(<111>//normal direction (ND))-grains and led to strong γ-fiber recrystallization texture. By contrast, the prior big-grained microstructure gave rise to relatively fast recrystallization kinetics at the early stage due to the diversified nucleation orientation and rapid grain growth in the interior of coarse deformed γ-grains with the help of in-grain shear bands. However, relatively slow kinetics was displayed at the later stage because the coarse deformed λ(<001>//ND)-grains were sluggish to recrystallize. Hence, continuous recrystallization and shear bands induced nucleation contributed to strong λ-fiber texture. Magnetic induction B50 continuously improved as the prior grain size increased, while both the low-frequency core loss P15/50 and the high-frequency core loss P10/400 decreased firstly and then increased with different critical prior grain size.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering