Abstract:Highly conducting $SnO_{2}$ thin films were prepared by chemical spray pyrolysis technique. One set of as-deposited films were annealed in air for 2 h at 850$^{o}$C. These as-deposited and annealed films were irradiated using $Au^{9+}$ ions with energy of 120 MeV at different fluences ranging from $1\times10^{11}$ to $3\times10^{13}$ $ions/cm^{2}$. Electrical measurement shows that as-deposited $SnO_{2}$ films are in conducting state with n = $3.164 \times 10^{20}$ $cm^{-3}$ and annealed $SnO_{2}$ films are in insulating state. The amorphized latent tracks are created only above a certain threshold value of $S_{e}$, which directly depends on the free electron concentration (n). The electronic energy loss ($S_{e}$) of 120 MeV $Au^{9+}$ ions in $SnO_{2}$ is greater than the threshold energy loss ($S_{eth}$) required for the latent track formation in annealed $SnO_{2}$ thin film, but is less than $S_{eth}$ required for as-deposited $SnO_{2}$ film. Therefore, the latent tracks are formed in the annealed $SnO_{2}$ film and not in the as-deposited $SnO_{2}$ film. Thermal spike model is used for the calculation of threshold energy loss and radius of melted zone. The possible mechanism of the structural changes and surface microstructure evolutions is briefly discussed in the light of ion's energy relaxation processes and target's conductivity. The atomic force microscopy (AFM) study of films shows that the morphologies of irradiated films are linked with carrier concentration of target materials.

Micro and nano-patterning of single-crystal diamond by swift heavy ion irradiation

Role of Carrier Concentration in Swift Heavy Ion Irradiation Induced Surface Modifications

Focused-helium-ion-beam blow forming of nanostructures: radiation damage and nanofabrication

Process design for the manufacturing of soft X-ray gratings in single-crystal diamond by high-energy heavy-ion irradiation

Mechanisms of surface nanostructuring of Al2O3 and MgO by grazing incidence irradiation with swift heavy ions

Characterization of Single Crystal Diamond Damaged Layer Induced by Ion Implantation and Restored by Varying Annealing Conditions

Characterization of the recovery of mechanical properties of ion-implanted diamond after thermal annealing

Direct-write milling of diamond by a focused oxygen ion beam

Resolution, masking capability and throughput for direct-write, ion implant mask patterning of diamond surfaces using ion beam lithography

Characterization of Three-Dimensional Microstructures in Single Crystal Diamond

Ion irradiation induced structural modifications in diamond nanoparticles

Periodic nano ripple fabricated on diamond and its structure damage repair

Diamond-defect engineering of NV- centers using ion beam irradiation

Diamond Processing by Focused Ion Beam - Surface Damage and Recovery

Ion implantation in nanodiamonds: size effect and energy dependence

Tailored engineering of crystalline surface enabled by ion-irradiation-assisted femtosecond laser ablation

Swift heavy ion irradiation of SrTiO$_3$ under grazing incidence

Ultra-smooth single crystal diamond surfaces resulting from implantation and lift-off processes

Surface microstructuring of single crystalline diamond based on the accumulated energy homogenization in the nanosecond pulsed laser ablation

From groove to hillocks – Atomic-scale simulations of swift heavy ion grazing impacts on CaF 2

Spectroscopic measurement of the refractive index of ion-implanted diamond