Abstract:In this study, a hot isostatic pressing (HIP) manufactured SiC particles (SiC p ) reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite was fabricated through ball-milling, HIP, homogenization, hot extrusion, solution treatment, and aging treatment. The results showed the presence of an interfacial reaction layer, MgAl 2 O 4 , around the SiC p , which enhanced the bonding between the particles and the matrix. The aging treatment resulted in the formation of different aging precipitates, which were featured by GP zone for T4, GP zone + η' (metastable MgZn 2 ) + η (stable MgZn 2 ) for T6 and GP zone + η' (metastable MgZn 2 ) for T6I4. The composite samples of T4, T6, and T6I4 exhibited different mechanical properties. Specifically, the elastic modulus was measured as 102.9, 103.4, and 102.3 GPa, the yield strength was 685.3, 598.1, and 619.7 MPa, the ultimate tensile strength was 713.6, 618.9, and 633.3 MPa, and the elongation was 2.2%, 1.8%, and 2.8%, respectively. Furthermore, the corrosion behavior of the composite was evaluated through electrochemical, intergranular corrosion, and exfoliation corrosion. The corrosion current density was found to be 3.17 × 10 −7 , 4.97 × 10 −7 , and 3.67 × 10 −7 A cm −2 , the corrosion potential was measured as −0.70, −0.81, and −0.56 V, and the maximum intergranular corrosion depth was 139.9, 167.8, and 106.2 μm for T4, T6, and T6I4, respectively. The severity of exfoliation corrosion varied, with T4 showing severe pitting, T6 exhibiting moderate pitting, and T6I4 displaying slight pitting. The strengthening mechanism and load transfer strengthening of the composites were discussed in detail based on theoretical calculations, and the anti-corrosion mechanisms were also analyzed.

Comparative analysis of phase composition and heat resistance of piston silumin and experimental alloy Al4Cu2Mn0·5Ca0·2Zr (wt. %)

Effects of Alloying Elements and Temperature on Thermodynamic State and Microstructure of Piston Aluminum Alloy

Microstructural and thermal properties of piston aluminum alloy reinforced by nano-particles

Microstructure and Coefficient of Friction of Silumins Obtained by Rapid Solidification

Microstructural Evolution and Tensile Properties of Al-Si Piston Alloys during Long-Term Thermal Exposure

Experiment and numerical simulation study of thermal fatigue of an aluminum alloy piston

Influence of Cu/Mg Ratio and Content on Heat-Resistance of Al–Cu–Mg Alloys

Morphological Evolutions of Ni-Rich Phases in Al-Si Piston Alloys during 250–400 °C Thermal Exposure Processes

New High Strength and Heat Resistance Aluminum Alloy Material for Engine Cylinder Head

Analysis of Properties for in Situ Al(2)O(3)p/A356 Composites Synthesised from the Al-SiO2 System

Microstructure and Mechanical Properties of In-Situ Α-Al2o3p/al-12si Composites Fabricated by Direct Melt Reaction Method with Aid of Electromagnetic Stirring

Influence of the Al Content on the Properties of Mechanically Alloyed CoCrFeNiMnXAl20-X High-Entropy Alloys

Strengthening Mechanism and Thermal Deformation Behavior of Al-12Si/Fe Piston Composite

Microstructure and properties of a HIP manufactured SiC p reinforced high alloyed Al–Zn–Mg–Cu–Zr–Ti aluminum matrix composite

Microstructure, Phase Formation and Heat-Treating of Novel Cast Al-Mg-Zn-Cu-Si Lightweight Complex Concentrated Aluminum Based Alloy

Comparative analysis on high temperature tribological behaviour of additive manufactured and cast AlSi10Mg alloy

Double-stage Hardening Behavior and Fracture Characteristics of a Heavily Alloyed Al–Si Piston Alloy During Low-Cycle Fatigue Loading

Microstructural evolution and mechanical properties of cast Al‐2.6Li‐2.8Mg‐(0.5, 1.4)Cu‐0.2Zr‐0.2Sc alloys during heat treatment

Tribotechnical Properties of Cu–Al Antifriction Gas Thermal Coatings in Liquid and Grease Lubricants

Optimization of the Composition and Structure of Deformable Heat Resistant Aluminum Alloy

Manufacturing Feasibility of All-Aluminum Automotive Engines Via Application of High Silicon Aluminum Alloy