Abstract:Background: Tungsten (W) is a promising candidate for future use in fusion reactors as plasma facing material. During operation it will be exposed to both particle irradiation and high heat flux (HHF) loads. Particle irradiation, especially helium (He), is expected to cause significant surface modifications of W, might leading to performance degradation. The effect of heat loading can accelerate such surface damage. Therefore, the performance of W under the combined action of both heat and particle fluxes has to be investigated in more detail.Purpose:The aim is to investigate the surface modifications of rolled W during exposure to combined heating and He particle flux depending on surface temperature, He flux and fluence.Methods: The He-flux/heating experiments were performed on rolled W samples using the neutral beam HHF test facility GLADIS at IPP Garching, Germany. HHF loads generated with He atoms of 2.4 MW·m?2 and 9.5 MW·m?2 were used. W samples were adiabatically loaded to peak surface temperatures of ~1000 K, ~2000 K and ~3000 K, close to melting. He fluences increased from about 1×1021m?2 to 6×1022 m?2.Results: During He-loading at a low surface temperature (~1000 K), with increasing fluence, defects appeared in grains first, and then blistering was observed on the sample surface, with many ruptured blisters to form lids and grooves. The largest blisters formed on grains with near <001> surface normal. As fluence was increased continuously, small holes were formed on the surface, and the grooves still existed. However, at intermediate surface temperature (~2000 K), with increasing fluence, the damage morphology changed from a porous structure with blisters,via a porous structure with grooves, to a small coral-like structure. At high surface temperature (~3000 K), an evolution from a porous structure to a coral-like structure with increasing fluence was observed, and the coral-like structure changed little as the increasing of fluence continuously. It is shown that the surface modification of rolled W is dependent on a competitive relationship between the formation of blisters and coral-like structures. To study the behaviour of such He damaged surfaces under fusion relevant transient heat loads, 0.9GW·m?2 Edge Localized Modes (ELMs)-like laser thermal shocks were applied. Local melting was observed on the coral-like structure after thermal shocks.Conclusion: The damage morphology of rolled W changes from blisters with a grain orientation dependence to a porous/coral-like structure with increasing temperature, because at high temperatures the Hen and HenVm (He-vacancy) clusters will be broken up and He will diffuse relatively deeply into the W bulk. This transformation of damage morphology can also be induced by the rise of He fluence.

Helium load on W-O coatings grown by pulsed laser deposition

Deuterium loading of redeposited-like W coatings present in tokamaks by ion implantation

The Influence of Coherent Oxide Interfaces on the Behaviors of Helium (He) Ion Irradiated ODS W

Surface Modification of W–V Alloy Exposed to High Heat Flux Helium Neutral Beams

Helium induced nanoscopic morphology on tungsten under fusion relevant plasma conditions

Fuzz Nanostructure and Erosion on Tungsten–vanadium Alloys Exposed to Helium Plasma in the STEP Linear Plasma Device

Helium retention feature in the boron deposited layer on tungsten substrate by laser-induced breakdown spectroscopy and machine learning approach

Helium effects on the surface and subsurface evolutions in single-crystalline tungsten

Surface modifications of rolled W during exposure to high heat loads with He

Response of tungsten surfaces to helium and hydrogen plasma exposure under ITER relevant steady state and repetitive transient conditions

Helium retention depth profile in plasma-facing materials measured by glow-discharge optical emission spectroscopy

Helium plasma immersion ion implantation studies of tungsten and tungsten heavy alloys for fusion plasma facing components

Behavior of helium cavities in ion-irradiated W-Ni-Fe ductile-phase toughened tungsten

Surface Modification and Deuterium Retention of High Energy Rate Forging W-Y2O3exposed to Deuterium Plasma

Hardening and Strain Localisation in Helium-Ion-Implanted Tungsten

In situ measurements of low energy D plasma-driven permeation through He pre-damaged W

Blistering Behavior and Deuterium Retention in Tungsten Vanadium Alloys Exposed to Deuterium Plasma in the Linear Plasma Device STEP

Helium-Implantation-Induced Lattice Strains and Defects in Tungsten probed by X-ray Micro-diffraction

Tungsten Material Behavior under H2, D2, and He Plasma Interaction Conditions in the Framework of Fusion-Relevant Studies

Influence of impurity gas seeding into deuterium plasma on the surface modification, sputtering erosion and deuterium retention in W and W-La2O3 alloy

Enhanced radiation resistance of W-based HEA under helium-ion irradiation conditions