Abstract:As demand grows to replace petroleum-derived materials with more environmentally friendly materials, the use of wood in high-performance applications in the automotive industry has received increasing attention. Understanding the behaviour of wood during forming processes is an essential step towards its successful implementation in the automotive sector. This study accordingly investigates the compressive response and failure behaviour of two hardwood species (beech and birch) at different moisture and temperature levels. The experimental tests were conducted at 20, 60, 100 and 140 °C on samples with various moisture levels, ranging from completely dry to wet conditions. The stress–strain curves were analysed, and the failure modes were examined using visual observations and microscopic analyses. The results demonstrated that, when beech and birch were tested in standard laboratory conditions, the dominant mode of failure was the kink band, where the fibres buckled in an approximately sigmoidal shape. However, when the wet wood was tested at temperatures of 60 °C and above, the stress–strain curves showed long stress plateau region as well as strain hardening. We hypothesise that, at elevated moisture and temperature levels, the cell walls, promoted by the improved flexibility of the polymer network, start to fold, hence, the load stabilises or even slightly decreases. This corresponds to the plateau stage in the stress–strain curves of beech and birch. With further loading, the distance between the folds becomes rather small and compaction of the folds (or densification) apears to occur, corresponding to the observed strain–hardening stage. This hypothsis is supported by the concertina-like folds seen in the scanning electron microscope (SEM) graphs of post-tested specimens. Here, we present and discuss the effect of rays, as well as cell wall/lumen ratio, on the compression behaviour of wood, and the stability of the forming process.

Moisture-induced Damage Evolution in Laminated Beech

A Waveform Clustering Method for Damage Mode Identification for Composite Laminates under Hygrothermal Environment

Finite Element Analysis of a Modified Progressive Damage Model for Composite Laminates under Low-Velocity Impact

Numerical Investigation on the Repeated Low-Velocity Impact Behavior of Composite Laminates

Modeling of Damage Evolution in Soft-Wood Perpendicular to Grain by means of a Discrete Element Approach

Damage modes detection of composite laminates using improved modal strain energy method

Compressive Experiment and Damage Simulation of A Composite Structure with Ply Drop-Off

Microscopic Progressive Damage Simulation and Scale-Span Analysis of Cross-Ply Laminate Based on the Elastic–Plastic Theory

Damage Analysis of Composite Laminate with Large Open-hole under Compression Using 3D Strain Progressive Damage Theory

Tensile Progressive Damage and Compressive Postbuckling Analysis of Open-Hole Laminate Composites

Micromechanical experiments of interlaminar deformation and damage in angle-ply thermoplastic composite laminates

Prediction of moisture-induced cracks in wooden cross sections using finite element simulations

Moisture Effects on Acoustic Emission Characteristics and Damage Mechanisms of Balsa Wood Core Composite Sandwich under 4-Point Bending

Micro-mechanical Analysis of Matrix Crack-Induced Delamination in Cross-Ply Laminates in Tension

Micromechanical Experiments of Interlaminar Deformation and Damage in Quasi-Isotropic Thermoplastic Composite Laminates

Dependence of damage modes on the ply-thickness of ultra-thin-ply composites

The compressive behaviour of beech and birch at different moisture and temperature conditions along the grain

Rheological Model for Wood

Moisture-dependent, viscoelastic creep of European beech wood in longitudinal direction

Micromechanical Progressive Damage Analysis of Inter- and Intra-Layer Failures in Fiber-Reinforced Composite Laminates

Damage Evolution and Multi-Scale Analysis of Carbon Fiber-Reinforced Cross-Ply Laminate with Thermal Residual Stress