Abstract:Selective catalytic reduction technology is the most commonly used method for NOx control, but the preparation process of the catalysts is complicated and the preparation cost is high. In this study, a novel low-cost catalyst for selective catalytic reduction of nitrogen oxides was prepared by treating vanadium-bearing steel slag with calcination modification and sulfuric acid modification. The activity test results show that the calcination modification can slightly improve the high-temperature activity of the catalysts. Among acid-modified catalysts, sulfuric acid modification can greatly improve the denitration activity of the catalyst, and calcination of the catalyst before sulfuric acid modification can obtain a higher activity denitration catalyst. The NOx removal efficiency of VSS-C-S catalyst reached 82.4% at 250°C. In addition, the catalyst modified with sulfuric acid after calcination has better water and sulfur resistance and regeneration performance. In the case of high water vapor and sulfur dioxide concentration, its denitration efficiency is 62.5%. The characterization results show that both calcination modification and sulfuric acid modification can promote the formation of α-Fe2O3, but calcination modification reduces the specific surface area and redox capacity of the catalysts. The sulfuric acid modification can form a new pore structure and a large number of sulfate species on the catalyst surface, and improve the existing state of vanadium species in the catalysts. The specific surface area of VSS-C-S catalyst is 43.90m2·g-1. Meanwhile, the adsorbed oxygen content of VSS-C-S catalyst is 24% higher than that of VSS-S-5 catalyst. It shows that the modification effect of sulfuric acid can be better exerted by calcination first and then modification with sulfuric acid. The results of in-situ DRIFTS experiments show that the NH3-SCR reaction of the calcined modified catalyst mainly follows the L-H mechanism. The NH3-SCR reaction of sulfuric acid-modified catalysts mainly follows the E-R mechanism. The active sites on the VSS-C-S catalyst surface adsorb a large amount of NH3 species and activate them as NH2 active intermediates, which directly react with gaseous NO. Therefore, the catalyst modified with sulfuric acid after calcination has higher activity. The work provides a novel idea for reducing catalysts cost and promoting cleaner production.

Preparation and Application of Slag‐Based Catalyst for Steelmaking

Effect of M (M = Fe, Co, Ni, Cu, Ce) loaded on blast furnace slag and its application in low‐temperature NH3‐SCR

Study on Denitration Performance of Solid Waste Blast Furnace Slag Catalysts under Different Preparation Processes

Ultrasonication-Assisted Preparation of a Mn-Based Blast Furnace Slag Catalyst: Effects on the Low-Temperature Selective Catalytic Reduction Denitration Process

Recycling of manganese ore desulfurization slag for preparation of low-temperature NH 3 -SCR catalyst with good scale-up production performance

Economic and Carbon Emission Analysis of Two Typical Denitrification Systems for Sintering Process in the Iron and Steel Industry

The effect of basicity of modified ground granulated blast furnace slag on its denitration performance

Manganese-cerium oxide (MnOx-CeO2) catalysts supported by titanium-bearing blast furnace slag for selective catalytic reduction of nitric oxide with ammonia at low temperature

Application of a blast furnace slag carrier catalyst in flue gas denitration and sulfur resistance

Vanadium-bearing steel slag catalysts for selective catalytic reduction of NOx by NH3

Application of manganese-containing soil as novel catalyst for low-temperature NH3-SCR of NO

Mechanochemical activation of titanium slag for effective selective catalytic reduction of nitric oxide

Harmless Treatment of Waste Selective Catalytic Reduction Catalysts During Iron Ore Sintering Process

Research on deeply modified Fenton sludge for the selective catalytic reduction of NO x : Promotion mechanism of acidification reorganization

Feasibility of Preparing Steel Slag–Ground Granulated Blast Furnace Slag Cementitious Materials: Synergistic Hydration, Fresh, and Hardened Properties

The Enhanced Resistance to Na+-poisoning of MnCoCrOx SCR Catalyst by Acidity Regulation: the Mechanism of Sulfuric Acid Pretreatment

Surface microstructure of magnetic blast furnace dust and its correlation with persulfate catalytic performance: Laying foundation for its innovative applications as a catalyst precursor

Insight into blast furnace dust for selective catalytic reduction of NOx: An experimental and DFT study

Removal of SO2 from flue gas using blast furnace dust as an adsorbent

Gd-Mn-Ti Composite Oxides Anchored on Waste Coal Fly Ash for the Low-Temperature Catalytic Reduction of Nitrogen Oxide

SELECTIVE REDUCTION DENITRIFICATION OF FLUE GAS BY USING CATALYST Ag/Al2O3 AND REDUCING AGENT C3H6