Highly Foldable, Super-Sensitive, and Transparent Nanocellulose/Ceramic/Polymer Cover Windows for Flexible OLED Displays
Jingyi Xie,Dongmei Jia,Mahmut Dirican,Yi Xia,Chunxing Li,Yi Liu,Meng Cui,Chaoyi Yan,Jiayu Wan,Hao Liu,Gang Chen,Xiangwu Zhang,Jinsong Tao
DOI: https://doi.org/10.1021/acsami.2c01353
2022-03-30
Abstract:Polymer cover windows are important components of flexible OLED displays but they easily generate wrinkles because of their weak folding resistance. Increasing the polymer thickness can improve the folding resistance but it decreases the touch sensitivity. Thus, fabricating highly foldable and supersensitive polymer cover windows is still challenging. Here, by incorporating cellulose nanocrystals (CNCs) and zirconia (ZrO2) into colorless polyimide (CPI), we developed a highly foldable and supersensitive hybrid cover window. Inspired by the theory of elasticity, we added rigid CNCs into CPI to improve the elastic modulus and hence the foldability. ZrO2 was introduced to improve dielectric properties, which leads to improved touch sensitivity. After these modifications, the elastic modulus of the cover windows was increased from 1432 to 2221 MPa, whereas its dielectric constant was increased from 2.95 to 3.46 (@1 × 106 Hz), resulting in significantly enhanced foldability and sensitivity. Meanwhile, because of the nano size of CNCs and ZrO2, the hybrid cover windows exhibit excellent optical properties with the transmittance of ∼88.1%@550 nm and haze of 2.39%. With improved and balanced mechanical, dielectric, and optical properties, these hybrid cover windows overcome current cover windows' defects and could be widely used in next-generation flexible displays.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.2c01353.Scheme S1, schematic illustration of the synthesis procedure of the CPI; Figure S1, stress–strain curves of CNC; Figure S2, stress–strain curve of ZrO2/CPI and CNC/ZrO2/CPI with different ZrO2 and 1 wt % CNC loadings; Figure S3, pencil hardness of CPI, 3% ZrO2/CPI, and 3% CNC/ZrO2/CPI; Figure S4, nanoindentation characterization of the CPI, 3% ZrO2/CPI, and 3% CNC/ZrO2/CPI; Figure S5, schematic image of the folding test with an inward folding radius of 3 mm; Figure S6, magnified micrographs of cross sections of pure CPI, 3% ZrO2/CPI, and 3% CNC/ZrO2/CPI (PDF)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology