Realization of Highly Foldable Conductive Substrates with 2000 Cyclic Mechanical Stability through Silver Nanowires/Cellulose Structure Design

Pengfei Li,Hongjiang Li,Runfei Wang,Renjie Miao,Lei Qian,Xuan Feng,Weiyan Wang,Jia Li,Weijie Song

DOI: https://doi.org/10.1021/acsaelm.1c00247

IF: 4.494

2021-05-12

ACS Applied Electronic Materials

Abstract:Foldable electronics, with the advantages of size compactness and shape transformation, are promising for portable and wearable applications. The challenge for realizing foldable devices is exploiting highly foldable conductive substrates free from deformation under large strain. In this work, highly foldable and degradable transparent conductive substrates were constructed using ∼20 μm ultrathin regenerated cellulose film (RCF) substrates to reduce strain, embedding silver nanowires (AgNWs) into RCFs to improve the interface binding force, as well as improving the adhesive strength of AgNWs junction. The AgNWs/RCF complex with an initial sheet resistance of 14 Ω/sq maintained an electrical conductivity after either single folding for 2000 cycles or double folding for 1000 cycles. Moreover, the difference in the electrical characteristics of AgNWs/RCF after single folding with +180 and −180° angles as well as double folding was explained to be related to the different microstructure deformations. Lastly, the first foldable polymer-dispersed liquid crystals devices using the AgNWs/RCF conductive substrates were demonstrated with 1400 cyclic stability. Our work paves the way toward realizing highly foldable transparent electrodes for foldable displays and detectors and wearable device applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsaelm.1c00247?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsaelm.1c00247</a>.Characteristic stress–strain curve for RCF (Figure S1); photographs of RCF after being immersed in different organic solvents for 24 h (Figure S2); SEM images of RCF and AgNWs/RCF after immersion in water for 12 h (Figure S3); SEM morphological image of AgNWs/glass (Figure S4); sheet resistance of AgNWs/glass and AgNWs/RCF (Figure S5); change in the resistance of AgNWs/RCF electrodes as a function of the folding cycle of single folding with +180° (Figure S6); change in the resistance of AgNWs/RCF, AgNWs-RCF, and AgNWs/CNF electrodes as a function of (a) folding cycle and (b) sticking cycle (Figure S7); photographs of the PDLC devices attached to the corner of a square box at <i>V</i>_off (0 V) and <i>V</i>_on (25 V) (Figure S8); and comparison of PDLC devices on AgNWs/RCF with other reported flexible PDLC devices (Table S1) (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.1c00247/suppl_file/el1c00247_si_001.pdf">PDF</a>)Dynamic process of folding the PDLC devices (Video) (<a class="ext-link" href="/doi/suppl/10.1021/acsaelm.1c00247/suppl_file/el1c00247_si_002.mp4">MP4</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,engineering, electrical & electronic