Electropulses induced direct aging and ultrafast precipitation in additive manufactured 15-5 PH stainless steel
Binghua LvSheng CaoXiaodong NiuHong LuoBoris StraumalYuanshen Qia Department of Materials Science and Engineering,Guangdong Technion – Israel Institute of Technology,Shantou,People's Republic of Chinab Department of Mechanical Engineering,College of Engineering,Shantou University,Shantou,People's Republic of Chinac Institute for Advanced Materials and Technology,University of Science and Technology Beijing,Beijing,People's Republic of Chinad Osipyan Institute of Solid State Physics,Russian Academy of Sciences,Chernogolovka,Russiae Department of Materials Science and Engineering,Technion – Israel Institute of Technology,Haifa,Israelf Guangdong Provincial Key Laboratory of Materials and Technology for Energy Conversion,Shantou,People's Republic of China
DOI: https://doi.org/10.1080/21663831.2024.2352052
2024-05-19
Materials Research Letters
Abstract:Periodic electric current pulses, i.e. electropulses, were applied on selective laser melting prepared 15-5 precipitation hardening stainless steel for direct aging. Traditional aging treatment typically takes hours to achieve peak hardening and could induce reverted austenite. Herein, electropulsing treatment on as-built sample can dramatically reduce the processing time to 6 min. Moreover, the nucleation of reverted austenite triggered by the segregation of Ni atoms on the interfaces between Cu-rich precipitates and martensite was not observed. These two unique phenomena were rationalized to the unsynchronized enhancement of diffusivity of Cu and Ni atoms under electropulses due to their different electron configurations. Electropulsing treatment selectively boosted the diffusivity of Cu atoms in additive manufactured maraging stainless steel and dramatically reduced the direct aging time from hours to minutes without inducing reverted austenite.
materials science, multidisciplinary