Strengthening and Reinforcing of Ceramic-Metallic Materials by Quaternary Solid Solutions of Metallic Phases During Spark Plasma Sintering
A. V. Hmelov,Hmelov, A. V.
DOI: https://doi.org/10.1007/s11148-023-00746-9
2023-08-03
Refractories and Industrial Ceramics
Abstract:The article shows the effect of mixtures of metal powders of Ti, Nb, Cr, Zr and Ti, Mo, Cr, V, as well as Mo, Nb, Cr, and Ta during spark plasma sintering of compositions at a pressing load of 85 MPa in the range of 1200 – 1600°C on the phase composition, microstructure, grains sizes of crystalline phases, relative density, linear shrinkage, physico-mechanical properties, linear correlation, values of standard deviations of the modulus of elasticity and fracture toughness of mullite–(Ti,Ta)(C,N)–B 4 C– c -BN samples. Synthesized powders of TiC, TiN, B 4 C, and h -BN are characterized by different intensity of crystallization of TiC, TiN, B 4 C, and h -BN phases, respectively. Spark-plasma sintered solid solution of (Ti,Ta)(C,N) shows intensive crystallization of the (Ti,Ta)(C,N) phase at 1500°C, as well as crystalline, uniform, and densely sintered microstructure. Sintered samples with the mixtures of metal powders show similar mullitization and crystallization of the (Ti,Ta)(C,N), B 4 C, and c -BN phases with different evolution of the crystalline β-Ti, Nb, Cr, Zr, β -Ti, Mo, Cr, V, and β -Mo, Nb, Cr, Ta phases in the range of 1200 – 1600°C. The microstructures of sintered samples are crystalline, variously uniform and variously densely sintered. The samples with mixtures of metal powders form variously dispersed granular compositions of crystalline phases in the range of 1200 – 1600°C, different uniformity, density, path, width of boundary layers of solid solutions of metallic phases, different packing of particles of non-oxide and solid solutions of metallic phases, have different path and width of propagating microcracks at the boundaries of ceramic particles and particles of solid solutions of metallic phases at 1300 and 1500°C, as well as across the boundary layers of solid solutions of metallic phases at 1500°C. This differently affects the ingrowth and values of physico-mechanical properties, crack resistance linear correlation, values of standard deviations of the modulus of elasticity and fracture toughness in the range of 1200 – 1600°C.
materials science, ceramics