Nanocomposite versus solid solution formation in the TiSiN system

Nina Schalk,Yvonne Moritz,Ganesh Kumar Nayak,David Holec,Christoph Hugenschmidt,Vassily Vadimovitch Burwitz,Lucian Mathes,Maximilian Schiester,Christian Saringer,Christoph Czettl,Markus Pohler,Christian Mitterer,Michael Tkadletz

DOI: https://doi.org/10.1016/j.actamat.2024.120063

IF: 9.4

2024-06-01

Acta Materialia

Abstract:This work contributes to the ongoing scientific debate on the structure of TiSiN coatings. In order to illuminate the formation of a nanocomposite structure versus the formation of a Ti 1-x Si x N solid solution, a series of TiSiN coatings was synthesized and the influence of varying N 2 pressures and the addition of Ar to the deposition atmosphere on the structure of TiSiN coatings was investigated in detail. The powdered TiSiN coatings all exhibited a lower lattice parameter than reported for TiN, which further decreased with increasing N 2 pressure, at comparable elemental compositions. For all coatings the presence of a crystalline Ti 1-x Si x N solid solution as well as an amorphous SiN x phase fraction could be detected, where more Si was incorporated into the Ti 1-x Si x N solid solution at higher pressures, due to less energetic growth conditions and the additional kinetic activation stemming from Ar ions resulted in less Si incorporation. Density functional theory calculations showed that defects only play a subordinate role for the low observed lattice parameters.

materials science, multidisciplinary,metallurgy & metallurgical engineering