Odor-Reduced HDPE-Lignin Blends by Use of Processing Additives
Lok,Mueller,Buettner,Bartel,Erdmann
DOI: https://doi.org/10.3390/polym14132660
IF: 5
2022-06-30
Polymers
Abstract:The comprehensive use of natural polymers, such as lignin, can accelerate the replacement of mineral oil-based commodities. Promoting the material recovery of the still underutilized technical lignin, polyolefin-lignin blends are a highly promising approach towards sustainable polymeric materials. However, a limiting factor for high-quality applications is the unpleasant odor of technical lignin and resulting blends. The latter, especially, are a target for potential odor reduction, since heat- and shear-force intense processing can intensify the smell. In the present study, the odor optimization of kraft and soda HDPE-lignin blends was implemented by the in-process application of two different processing additives–5% of activated carbon and 0.7% of a stripping agent. Both additives were added directly within the compounding process executed with a twin screw extruder. The odor properties of the produced blends were assessed systematically by a trained human panel performing sensory evaluations of the odor characteristics. Subsequently, causative odor-active molecules were elucidated by means of GC-O and 2D-GC-MS/O while OEDA gave insights into relative odor potencies of single odorants. Out of 70 different odorants detected in the entirety of the sample material, more than 30 sulfur-containing odorants were present in the kraft HDPE-lignin blend, most of them neo-formed due to high melt temperatures during extrusion, leading to strong burnt and sulfurous smells. The addition of activated carbon significantly decreased especially these sulfurous compounds, resulting in 48% of overall odor reduction of the kraft blend (mean intensity ratings of 5.2) in comparison to the untreated blend (10.0). The applied stripping agent, an aqueous solution of polymeric, surface-active substances adsorbed onto a PP carrier, was less powerful in reducing neo-formed sulfur odorants, but led to a decrease in odor of 26% in the case of the soda HDPE-lignin blend (7.4). The identification of single odorants on a molecular level further enabled the elucidation of odor reduction trends within single compound classes. The obtained odor reduction strategies not only promote the deodorization of HDPE-lignin blends, but might be additionally helpful for the odor optimization of other natural-fiber based materials.
polymer science