Surface Modification Of Linear Low-Density Polyethylene Film By Amphiphilic Graft Copolymers Based On Poly(Higher Alpha-Olefin)-Graft-Poly(Ethylene Glycol)
Zhisheng Fu,Min Liu,Junting Xu,Qi Wang,Zhiqiang Fan
DOI: https://doi.org/10.1002/app.32819
IF: 3
2011-01-01
Journal of Applied Polymer Science
Abstract:In this article, a series of amphiphilic graft copolymers, namely poly(higher alpha-olefin-co-para-methylstyrene)-graft-poly(ethylene glycol), and poly(higher alpha-olefin-co-acrylic acid)-graft-poly(ethylene glycol) was used as modifying agent to increase the wettability of the surface of linear low-density polyethylene (LLDPE) film. The wettability of the surface of LLDPE film could be increased effectively by spin coating of the amphiphilic graft copolymers onto the surface of LLDPE film. The higher the content of poly(ethylene glycol) (PEG) segments, the lower the water contact angle was. The water contact angle of modified LLDPE films was reduced as low as 25 degrees. However, the adhesion between the amphiphilic graft copolymer and LLDPE film was poor. To solve this problem, the modified LLDPE films coated by the amphiphilic graft copolymers were annealed at 110 degrees for 12 h. During the period of annealing, heating made polymer chain move and rearrange quickly. When the film was cooled down, the alkyl group of higher alpha-olefin units and LLDPE began to entangle and crystallize. Driven by crystallization, the PEG segments rearranged and enriched in the interface between the amphiphilic graft copolymer and air. By this surface modification method, the amphiphilic graft copolymer was fixed on the surface of LLDPE film. And the water contact angle was further reduced as low as 14.8 degrees. The experimental results of this article demonstrate the potential pathway to provide an effective and durable anti-fog LLDPE film. (C) 2010 Wiley Periodicals, Inc. J Appl Polym Sci 119: 1111-1121, 2011