Surface modification of LLDPE film with reactive hindered amine by photo-grafting copolymerization
Xiaoxuan Liu,Linghai Xie,Weiqun Zhang,Yanping Xu,Guangguo Wu,Laixing Xing Pang,Jianwen Yang,Zhaohua Zeng,Yonglie Chen
2003-01-01
Abstract:The surface modification by the photografting of r-HALS (reactive hindered amine light stabilizer) on a commercial polyolefin thin film was studied. The process proceeded by photo-initiated grafting copolymerization of 4-methacryloyloxy-1,2,2,6,6-pentamethyl-piperidine (MPMP), a reactive HALS, onto the surface of linear low density polyethylene(LLDPE) thin film, presoaked in the benzene solution containing benzophenone (BP) initiator and MPMP monomer and UV irradiation for short time under nitrogen atmosphere. All measurements of the grafted polymer surface, such as (relative intensity (R.I.) of ESCA lines C1S, O1S, or N1S, and Carbonyl Value (CV) or R.I. of FTIR-ATR spectral lines of carbonyl absorbance of MPMP, and the Yellowness Index (YI) of grafted LLDPE film have been performed. The grafting yield of MPMP onto the surface of LLDPE film was calculated by the weight gain of the sample after irradiation. The results show that the increase of carbonyl absorbance (or CV) was in line with the concentration of MPMP monomer in the presoaking solution, the grafting yield and the irradiating time. The N 1s signals in ESCA spectra of the grafted LLDPE surface clearly indicates that photo-grafted copolymerization has taken place and a distinct grafted layer on the surface produced. Yellowness Index (YI) of the grafted LLDPE films is much lower than that of the blank film through the 4500 hours photo-oxidation, an evidence for improvement of the photo-stability. Surface modification of LLDPE film by photo-grafted with r-HALS monomer has thus been proved efficient for the photostabilization of LLDPE.