Fluorinated acrylate-grafted LDPE films from UV-induced photograft polymerization

Bin Li,Wenguang Chen,Xiaogong Wang,Qixiang Zhou

DOI: https://doi.org/10.3321/j.issn:1000-3304.2002.06.017

2002-01-01

Acta Polymerica Sinica

Abstract:One kind of fluorinated acrylate monomer, R5610, was grafted onto the surface of LDPE films by UV-induced photograft polymerization. The existence of a fluorinated polymer layer and its linkage with the LDPE substrate through chemical bonds were confirmed by FTIR, ESCA, SEM and DSC measurements on the butanone-extracted grafted films. It's found that a moderate increase of the UV intensity, concentration of both photoinitiator and monomer, and reaction temperature favored the improvement of grafting yield. The overall activation energy for the photograft polymerization reaction of R-5610 on LDPE was calculated to be 54.2 kJ/mol. The surface contact angles of the grafted films were found to increase with the improvement of grafting yield before they became constant, which implied that there could be a boundary layer that influenced the interaction between the LDPE substrate and the probe water drops during the measurement of contact angles. The LDPE substrate interacted with the probe water drop through the boundary when grafting yield of the grafted film was low and the grafted polymer layer was thinner than the critical boundary thickness, which resulted in the similarity between contact angles of LDPE and grafted film. As grafting yield increased, the grafted polymer layer became thicker and the interaction between LDPE substrate and probe water drop was weakened, so the influence of fluorinated polymer on the contact angle became more remarkable and caused the increase of contact angle. When grafting yield went further higher and the thickness of grafted polymer layer exceeded the critical boundary thickness, the interaction between LDPE substrate and probe water drops disappeared, and the contact angle became stabilized thereafter as a result of fluorinated polymer becoming the only one to influence contact angle of grafted films.