Abstract:The scattering mechanisms governing the transport properties of high mobility AlInN/AlN/GaN two-dimensional electron gas (2DEG) heterostructures with various AIN spacer layer thicknesses from zero to 2 nm were presented. The major scattering processes including acoustic and optical phonons, ionized impurity, interface roughness, dislocation and alloy disorder were applied to the temperature-dependent mobility data. It was found that scattering due mainly to alloy disorder limits the electron mobility for samples having spacer layer thicknesses up to 0.3 nm. On the other hand, alloy scattering is greatly reduced as the AlN spacer layer thickness increases further, and hence the combination of acoustic, optical and interface roughness become operative with different degrees of effectiveness over different temperature ranges. The room-temperature electron mobility was observed to increase gradually as the AlN spacer layer increases. A peak electron mobility of 1630 cm(2) V-1 s(-1) was realized for the sample consisting of a 1 nm AlN spacer layer. Then, the electron mobility decreased for the sample with 2 nm AlN. Moreover, the measured 2DEG densities were also compared with the theoretical predictions, which include both piezoelectric and spontaneous polarization components existing at AlN/GaN interfaces. The experimental sheet carrier densities for all AlInN/AlN/GaN HEMT structures were found to be in excellent agreement with the theoretical predictions when the parasitic (unintentional) GaN layer deposited between AlN and AlInN was taken into account. From these analyses, 1 nm AlN spacer layer thickness is found to be the optimum thickness required for high electron mobility and hence low sheet resistance once the sheet carrier density is increased to the theoretically expected value for the sample without unintentional GaN layer.

Layer interdependence of transport in an undoped electron-hole bilayer

Transport and drag in undoped electron-hole bilayers

Theoretical Study of Electronic Transport in Two-Dimensional Transition Metal Dichalcogenides: Effects of the Dielectric Environment

Josephson-like tunnel resonance and large Coulomb drag in GaAs-based electron-hole bilayers

Two-Carrier Model-Fitting of Hall Effect in Semiconductors with Dual-Band Occupation: A Case Study in GaN Two-Dimensional Hole Gas

Electronic Transport in Disordered Bilayer and Trilayer Graphene

Low-temperature Mobility of Two-Dimensional Electron Gas in Selectively Doped Pseudomorphic N-AlGaAs/GaInAs/GaAs Structures

The effect of AlN interlayer thicknesses on scattering processes in lattice-matched AlInN/GaN two-dimensional electron gas heterostructures

Transport Measurements on Ultra-Clean Dual-Gated Suspended Bilayer Graphene

Resistive Signature of Excitonic Coupling in an Electron-Hole Double Layer with a Middle Barrier

Effects of Interchannel Coupling in A Two-Dimensional Electron Gas at High Magnetic Fields

Electronic Cooling Via Interlayer Coulomb Coupling in Multilayer Epitaxial Graphene

Electronic Transport in Two Stacked Graphene Monolayers.

Dielectric Environment Effect on Carrier Mobility of Graphene Double-Layer Structure

Energy Transfer Rate in Double-Layer Graphene Systems: Linear Regime

Inter-layer Edge Tunneling and Transport Properties in Double-Layer Quantum Hall Systems

Carrier scattering, mobilities and electrostatic potential in mono-, bi- and tri-layer graphenes

Anomalous Interlayer Transport of Quantum Hall Bilayers in the Strongly Josephson-Coupled Regime

Transport Measurement of Landau Level Gaps in Bilayer Graphene with Layer Polarization Control

Interplay Between Coherent and Incoherent Transport in Quantum Hall Bilayers

Electron-hole pairing in graphene-GaAs heterostructures