Abstract:The MgB2 coated superconducting tapes have been fabricated on textured Cu (0 0 1) and polycrystalline Hastelloy tapes using coated conductor technique, which has been developed for the second generation high temperature superconducting wires. The MgB2/Cu tapes were fabricated over a wide temperature range of 460-520 °C by using hybrid physical-chemical vapor deposition (HPCVD) technique. The tapes exhibited the critical temperatures (Tc) ranging between 36 and 38 K with superconducting transition width (\DeltaTc) of about 0.3-0.6 K. The highest critical current density (Jc) of 1.34 \times 105 A/cm2 at 5 K under 3 T is obtained for the MgB2/Cu tape grown at 460^{\circ}C. To further improve the flux pinning property of MgB2 tapes, SiC is coated as an impurity layer on the Cu tape. In contrast to pure MgB2/Cu tapes, the MgB2 on SiC-coated Cu tapes exhibited opposite trend in the dependence of Jc with growth temperature. The improved flux pinning by the additional defects created by SiC-impurity layer along with the MgB2 grain boundaries lead to strong improvement in Jc for the MgB2/SiC/Cu tapes. The MgB2/Hastelloy superconducting tapes fabricated at a temperature of 520 °C showed the critical temperatures ranging between 38.5 and 39.6 K. We obtained much higher Jc values over the wide field range for MgB2/Hastelloy tapes than the previously reported data on other metallic substrates, such as Cu, SS, and Nb. The Jc values of Jc(20 K, 0 T) \sim5.8 \times 106 A/cm2 and Jc(20 K, 1.5 T) ~2.4 \times 105 A/cm2 is obtained for the 2-\mum-thick MgB2/Hastelloy tape. This paper will review the merits of coated conductor approach along with the HPCVD technique to fabricate MgB2 conductors with high Tc and Jc values which are useful for large scale applications.

Hollow carbon spheres as an efficient dopant for enhancing critical current density of MgB2 based tapes

Enhancement of the Critical Current Density and the Irreversibility Field in Maleic Anhydride Doped MgB2 Based Tapes

Strongly enhanced critical current density in Fe-sheathed MgB2 tapes by stearic acid and stearate doping

Strongly Enhanced Critical Current Density in Mgb2/Fe Tapes by Stearic Acid and Stearate Doping

Significant Improvements of the High-Field Properties of Carbon-Doped MgB2 Films by Hot-Filament-assisted Hybrid Physical–chemical Vapor Deposition Using Methane As the Doping Source

Effect of Nano-C Doping on the In-Situ Processed MgB2 Tapes

Effect Of Nanoscale C And Sic Doping On The Superconducting Properties Of Mgb2 Tapes

Enhanced High-Field Performance in Fe-sheathed MgB2 Tapes Using Inexpensive Stearic Acid Additives

Effect of Various C Sources Co-Doping on Transport Critical Current Density and Grains-Connectivity of MgB2/Fe Tapes

The Effect of Zrsi2 and Sic Doping on the Microstructure and J(C)-B Properties of Pit Processed Mgb2 Tapes

Fabrication and Superconducting Properties of Nano-Sic Doped MgB 2 Tapes

Enhancement of Critical Current Density in MgB 2 Bulk with CNT-coated Al Addition

Influence of Oxygen Contents of Carbohydrate Dopants on Connectivity and Critical Current Density in Mgb2 Tapes

Strong enhancement of critical current density in MgB2 superconductor using carbohydrate doping

Effect of the processing parameters of MgB1.8(SiC)0.1/Fe tapes on the critical current density

MgB2 coated superconducting tapes with high critical current densities fabricated by hybrid physical-chemical vapor deposition

Effects of TiC Doping on the Upper Critical Field of MgB2 Superconductors

Effect of Nano-SiC and Nano-Si Doping on Critical Current Density of MgB 2

Enhanced superconducting properties of pre-doped B powder type MgB2 strands

Comparative Studies of Nanoscale SiC Whisker and Si/N/C Doped MgB2 Tapes

Nanoscale-SiC doping for enhancing Jc and Hc2 in the Superconducting MgB2