Abstract:Uni-directional carbon/carbon composites with high thermal conductivity are suitable to supply continuous thermal protection for future reentry vehicles since they could reduce surface temperature and ablation rates simultaneously in harsh environments. In this work, the high ther-mal conductivity carbon/carbon composites were prepared by chemical vapor infiltration. After heat-treatment, both their open porosity and internal friction increase due to the fiber/matrix ther-mal expansion mismatch;while their thermal conductive performance become better due to more complete carbon structure. With raising heat-treatment temperature from 1800 °C to 2450 °C, the mass and linear ablation rates of C/C composites with fibers vertical to the oxyacetylene torch for 60 s decrease from 0.66 mg/s and 2.95μm/s to 0.51 mg/s and 2.05μm/s respectively. The improved ablation resistance is resulted from the increased thermal conductivity from 282 to 508 W/(m·K) and more carbon fibers exposed to the flame during ablation, which have better oxi-dation resistance than those of carbon matrix. While such ablation rates become larger for compos-ites with fibers parallel to the flame, from 1.02 mg/s and 3.73μm/s to 1.28 mg/s and 5.01μm/s respectively since the ablation occurred more easily through gaps at the fiber/matrix interfaces, which become larger and are always exposed to the flame for this case.

The influence of heat treatment on the ablation behavior of the C/Cx-SiCy composites tested by thin-blade under oxyacetylene torch

Ablation behavior of thin-blade co-deposited C/Cx-SiCy composites under the influence of the complex fluid conditions of the oxyacetylene torch

Microstructure, Thermophysical Property and Ablation Behavior of High Thermal Conductivity Carbon/carbon Composites after Heat-Treatment

Ceramic Matrix Composite Cyclic Ablation Behavior under Oxyacetylene Torch

Optimized ablation resistance behavior and mechanism of C/SiC composites with high thermal conductive channels

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes

Ablation and mechanical behaviour of C/C composites under an oxyacetylene flame and tensile loading environment

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Ablation behavior of sharp leading-edge C/C-ZrC-SiC composites using 3000 C oxyacetylene torch

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation behaviors of ultra-high temperature ceramic composites

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Microstructure and Ablation Behavior of C/C-SiC-(ZrxHf1−x)C Composites Prepared by Reactive Melt Infiltration Method

Cyclic ablation behavior and microstructure evolution of multi-layer coating on C/C composites under oxyacetylene torch

Ablation behavior of C f /ZrC–SiC ultra–high temperature ceramic composites in oxyacetylene torch and plasma wind tunnel

Ablation Behavior of the SiC-Coated Three-Dimensional Highly Thermal Conductive Mesophase-Pitch-Based Carbon-Fiber-Reinforced Carbon Matrix Composite under Plasma Flame

Comparison of the ablation resistance of mullite modified C/C-SiC-HfC and C/C-SiC-HfC composites under oxyacetylene flame of 2.38 MW/m 2 heat flux

Ablation behavior and mechanisms of 3D-Cf/Ta0.8Hf0.2C-SiC composite at temperatures up to 2500 °C

Study on the ablation performance of SiC-coated high thermal conductivity three-dimensional C/C composites

Long-term ablation mechanisms of the YB4-Al2O3-Si3N4 modified Cf/HfC-SiC composites at 2600 °C