Abstract:Highlights • C/C-HfC-SiC sharp leading edges were prepared in near-net shape via precursor infiltration and pyrolysis. • The preferred sample possessed almost zero degradation at a temperature up to 2371 °C for 120 s. • The sharp leading edge with less SiC exhibited a remarkably low linear recession rate above 2500 °C. • The superior ablation resistance is attributed to the thermally stable oxide scale with oxygen barrier ability. HfC-SiC-modified carbon/carbon composite (C/C-HfC-SiC) sharp leading edges (SLEs) were prepared via precursor infiltration and pyrolysis for potential hypersonic applications. The effect of SiC proportion on the ablation behavior of the SLEs under oxyacetylene flames with 2.38 MW/m 2 and 4.18 MW/m 2 was investigated. The preferred sample with a volume ratio of HfC to SiC of 0.74 possessed almost zero degradation (linear recession rate 0.6 μm/s) up to a temperature of 2371 °C. As the temperature increases to 2527 °C in the latter condition, the SLE with less SiC (the volume ratio of HfC to SiC is 1.10) exhibited a linear recession rate of 1.03 μm/s during cyclic ablation of 3 × 40 s. Relatively more SiC addition is favorable under lower heat flux due to the better oxygen barrier performance of the scale. However, superior ablation resistance is available under higher heat flux with less SiC addition due to the higher thermal stability of the resulting oxide scale. Graphical abstract Download : Download high-res image (259KB) Download : Download full-size image

Ablation behavior of sharp leading-edge C/C-ZrC-SiC composites using 3000 C oxyacetylene torch

Cyclic ablation behavior of C/C–ZrC–SiC composites under oxyacetylene torch

Ablation performance of C/C-ZrC-SiC composites with in-situ YSi 2 -doped ZrC-SiC-ZrSi 2 coating under oxyacetylene torch

Ablation behavior of Cf/ZrC-SiC and Cf/SiC composites produced by precursor infiltration and pyrolysis combined with gaseous silicon infiltration

Ablation behavior of C f /ZrC–SiC ultra–high temperature ceramic composites in oxyacetylene torch and plasma wind tunnel

Ablation of advanced C/C-ZrC-SiC leading edge composites

Ablation behavior and mechanisms of ZrC-SiC-MoSi2 coated C/C-SiC-ZrC ceramic matrix composites under oxyacetylene torch

Ablation behaviour of the CVD-(ZrC/SiC)3 alternate coating on C/C composites under oxyacetylene torch with different heat fluxes

Ablation behavior of thin-blade co-deposited C/Cx-SiCy composites under the influence of the complex fluid conditions of the oxyacetylene torch

Ablation behavior of ZrC-SiC-ZrB2 and ZrC-SiC inhibited carbon/carbon composites components under ultrahigh temperature conditions

Ablation behavior of C/C–Zr1-xHfxC-SiC composites under an oxyacetylene flame at above 2500 °C

Ablation mechanism of C/C–SiC and C/C–SiC–ZrC composites in hypersonic oxygen-enriched environment

Ablation behaviors of ultra-high temperature ceramic composites

The influence of heat treatment on the ablation behavior of the C/Cx-SiCy composites tested by thin-blade under oxyacetylene torch

Microstructure and Ablation Performance of SiC–ZrC Coated C/C Composites Prepared by Reactive Melt Infiltration

Microstructure evolution and ablation mechanisms of Csf/ZrB2-SiC composites at different heat fluxes under air plasma flame

Long-term and cyclic ablation behavior of La2O3 modified Cf/ZrB2-SiC composites at 2500 °C

Ablation mechanism of Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC composite during plasma ablation above 2000 °C

Superior ablation resistance of C/C-HfC-SiC composite sharp leading edges above 2500 °C prepared by precursor infiltration and pyrolysis

Multi-cycle and long-term ablation behavior of Cf/ZrB2-SiC composites at 2500 °C

Ablation behavior of mullite modified C/C-SiC-HfC composites under oxyacetylene torch for single and cyclic ablations with two heat fluxes