Abstract:A natural mixture of heavy rare earths oxides extracted from xenotime mineral have been used to prepare large single crystals of high-temperature REBa2Cu3O(7-\delta) superconductor grown using the CuO-BaO self-flux method. Its mechanical properties along the ab-plane were characterized using instrumented indentation. Hardness and elastic modulus were obtained by the Oliver and Pharr method and corresponds to 7.4 \pm 0.2 GPa and in range 135-175 GPa at small depths, respectively. Increasing the load promotes the nucleation of lateral cracks that causes a decrease in hardness and the measured elastic modulus by instrumented indentation at higher loads. The indentation fracture toughness was estimated by measuring the radial crack length from cube-corner indentations at various loads and was 0.8 \pm 0.2 MPa.m1/2. The observed slip systems of REBa2Cu3O(7-\delta) single crystals were [100](001) and [010](001), the same as for YBa2Cu3O(7-\delta) single crystals. The initial stages of deformation and fracture in the indentation process were investigated. The hardness and elastic modulus were not strongly modified by the crystallographic orientation in the ab-plane. This was interpreted in terms of the resolved shear stresses in the active slip systems. Evidence of cracking along the {100} and {110} planes on the ab-plane was observed. As a conclusion, the mechanical properties of REBa2Cu3O(7-\delta) single crystals prepared from xenotime are equivalent to those of YBa2Cu3O(7-\delta) single crystals produced by conventional rare earths oxides.

Magnetic Penetration Depth and Surface Resistance in YBa_2Cu_3O_{7-delta}: New Results for Ultra High Purity Crystals

Nernst Effect And Superconducting Fluctuations In Zn-Doped Yba2cu3o7-Delta

Optical study of pair-breaking effect in Zn-substituted YBa2Cu3O7−δ

To appear in Physica C Growth of High Quality YBCO Single Crystals Using BaZrO 3 Crucibles

Superconducting Gap and Strong In-Plane Anisotropy in Untwinned YBa2Cu3O(7-delta).

Rare-earth ionic size effects on T-c in the series RBa2Cu3O7-delta

Anomalies In Transport Properties Due To The Normal-State Pseudogap In Doped Yba2(Cu1-Xmx)(3)O7-Delta(M = Co, Zn) Thin Films

STUDIES ON ANISOTROPY FOR SINGLE-CRYSTAL GdBa2Cu3O7-δ

Research on anisotropy for single crystal GdBa2Cu3O7−y

Flux Pinning in YBa2Cu3O7−δ Through Nanometer-Sized MgO Particles

In-Plane and Out-Of-Plane Magnetoresistivity in A Mtg Er-Doped Ybco Crystal

Ultrasonic Study on YBa2(Cu1−xZnx)3O7−δ

Characterization of the (cu,c)ba2ca3cu4o 11+δ Single Crystals Grown under High Pressure

Fabrication and Characterization for Single Crystal Substrates of YBa2Cu3O7 Δ and Related Materials

Depth-Sensing Indentation on REBa2Cu3O(7-δ) Single Crystals obtained from Xenotime Mineral

Yba2cu3o7-Delta Thin-Films with Bao Precipitates

Strong reduction of field-dependent microwave surface resistance in YBa$_{2}$Cu$_{3}$O$_{7-δ}$ with sub-micrometric BaZrO$_3$ inclusions

High-temperature Dielectric Properties of BaZr 0.8 Y 0.2 O 3-Δ Ceramics

Epitaxial YBa/sub 2/cu/sub 3/o/sub 7- Delta / Thin Films on LaMgAl/sub 11/o/sub 19/: New Substrates with Low Dielectric Losses

High Tc Superconductivity in Single Crystal YBa2Cu3O7−δ

Effect of the pseudogap on the mean-field magnetic penetration depth of YBCO thin films