NEUTRON DIFFRACTION STUDY ON Y-Ba-Cu-O
Baisheng Zhang,Chuntang Ye,Zhen Yang,Lan Jin,Shu Gan,Songlin Li,Huachen Hu,Xiangmiao Zheng,Fengxiang Chen,Wanjing Zhang,Chuanyi Li,Ke Wu,Kaixuan Chen
DOI: https://doi.org/10.1142/s0217979287000359
1987-01-01
Abstract:The structure of high Tc(88.7K) superconductor YBa2Cu3O7−δ has been studied at room temperature as well as at a temperature slightly below transition temperature by neutron powder diffraction technique. The room temperature data has been analysed using powder profile refinement based on the space group Pmmm. The structure parameters from the profile refinement are: lattice constants a=3.8033A, b=3.8737A , c=11.6275A with Y at 1h(0.5 0.5 0.5), Ba at 2t(0.5 0.5 0.1882), Cu-1 at 1a(0 0 0), Cu-2 at 2q(0 0 0.3565), O-1 at 2q(0 0 0.1600), O-2 at 2s(0.5 0 0.3767), O-3 at 2r(0 0.5 0.3795), O-4 at 1e(0 0.5 0) and O-5 at 1b(0.5 0 0). All sites except 2s, 1b, 1e are fully occupied; the refined populations for 2s, 1b, 1e are 1.74, 0.42, and 0.69 respectively, with Rp=8.40 , RI=5.21 . Thus, we get an oxygen deficiency δ=0.14 . It seems that no evidence for structural phase transition accompanying the superconducting transition was observed.