Formation mechanism of ultrafine grains at machined surface of 0.45 % carbon steel under high-speed turning process
Hyung-Won Park,Masaki Matsuda,Kanji Ishitaka,Shinichi Funase,Atsushi Tomizawa,Akira Hosokawa,Jun Yanagimoto,Takashi Ueda
DOI: https://doi.org/10.1016/j.jmapro.2024.01.071
IF: 5.684
2024-02-01
Journal of Manufacturing Processes
Abstract:Turning of 0.45 % carbon steel was performed with an Al 2 O 3 tool at a cutting speed of 64–923 m·min −1 to investigate the cutting behavior, such as cutting temperature, cutting force, and chip formation, and to clarify the formation mechanism of ultrafine grains at the machined surface under high-speed turning process. The principal force exhibited stable behavior at cutting speeds up to 923 m·min −1 . The cutting temperature exceeded 760 °C when the cutting speed was over 500 m·min −1 and reached 850 °C when the cutting speed was 923 m·min −1 . From the microstructure of machined surface, the shear band at all cutting speeds was observed at a depth of up to 20 μm. Discontinuous and continuous ultrafine ferrite and pearlite layers with nanosized grains at cutting speeds of 509 and 923 m·min −1 , respectively, were present at depths of up to 5–8 μm. Additionally, {211}〈111〉 and {110}〈112〉–{110}〈114〉 orientations in the ferrite were observed in an ultrafine layer, which are generally formed by shear-deformed austenites. From the results of finite element analysis at a cutting speed of 923 m·min −1 , the severe cutting affected zone was up to 10 μm, where the temperature, strain, and strain rate reached approximately 870 °C, 5, and 2 × 10 5 s −1 , respectively. Therefore, ultrafine ferrite and pearlite with nanosized grains could be formed owing to the α + Fe 3 C → γ → α + Fe 3 C phase transformation at the machined surface subjected to ultrahigh-speed and severe-shear thermomechanical processing.
engineering, manufacturing