Effect of added Ag on plasticity enhancement of Au80Sn20 eutectic alloys

Yufeng Huang,Wensheng Liu,Yunzhu Ma,Siwei Tang,Feng Xue,BaiShan Chen,Juan Wang

DOI: https://doi.org/10.1016/j.jallcom.2020.155849

IF: 6.2

2020-11-01

Journal of Alloys and Compounds

Abstract:Inherent brittleness greatly limits machining and applications of Au80Sn20 eutectic solder alloys. To overcome the frangibility of Au80Sn20 eutectic alloys, Ag was added to form novel Au78.44Sn19.6Ag1.96 alloy. The effects of 2 wt% Ag addition on the solidification microstructure and plastic deformation of Au80Sn20 eutectic alloys were then studied. The as-obtained Au78.44Sn19.6Ag1.96 exhibited excellent plastic deformation at room temperature. Ag was well-solubilized in Au5Sn phase to yield (Au,Ag)5Sn, eliminating secondary phase defects in Au5Sn. The point defects introduced by Ag reduced its stacking fault energy and enabled (Au,Ag)5Sn to initiate stacking faults and twinning. Moreover, the typical eutectic growth state of Au80Sn20 alloy was changed. AuSn phase in Au78.44Sn19.6Ag1.96 alloys showed preferential orientation in basal direction, leading to formation of basal-prismatic facets and providing basal slip at room temperature. The ability to coordinate deformation between both phases improved and room temperature plastic deformation reached above 60%. These findings can help steer possible future research regarding the deformation mechanism of fragile metals and provide practical guidance to increase the plasticity of fragile metals for solder manufacturing.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper aims to solve the inherent brittleness problem of Au80Sn20 eutectic alloy, which greatly limits its use in processing and applications. In order to overcome the brittleness of Au80Sn20 eutectic alloy, the researchers added silver (Ag) to it, forming a new Au78.44Sn19.6Ag1.96 alloy. By studying the influence of Ag addition on the solid - state microstructure and plastic deformation of Au80Sn20 eutectic alloy, the paper explores how to improve the room - temperature plasticity of this kind of alloy through micro - alloying technology, thereby improving its processing performance and industrial application range.

Specifically, the paper solves the problem through the following aspects:
1. **Microstructure change**: It studied how the addition of Ag changes the solid - state microstructure of Au80Sn20 alloy, especially how to eliminate the nano - scale defects in the Au5Sn phase and change the growth orientation of the AuSn phase.
2. **Plastic deformation mechanism**: It analyzed how the addition of Ag introduces point defects, reduces the stacking fault energy, and enables the (Au, Ag)5Sn phase to produce twinning deformation at room temperature, thereby coordinating the deformation ability between the two phases.
3. **Performance improvement**: Through the above mechanisms, a large - scale plastic deformation of Au78.44Sn19.6Ag1.96 alloy at room temperature has been achieved, and the plastic deformation ability has reached more than 60%.

These findings not only help to understand the deformation mechanism of brittle metals, but also provide practical guidance for improving the plasticity of brittle metals, especially in solder manufacturing applications.