Abstract:GEN3 steels are a new family of automotive sheet steels developed and commercialized in the last three years, specifically for body-in-white applications. The high ductility in GEN3 steels is typically achieved through the transformation-induced plasticity (TRIP) effect by the addition of silicon or aluminum. When these steels are formed into parts, the TRIP effect of austenite to martensite transformation provides enhanced ductility. Typically, 10 to 12 micrometers of zinc coating (known as galvanized coating) is applied to automotive steel sheets for corrosion protection. Liquid metal embrittlement (LME) cracking can occur during resistance spot welding (RSW) of galvanized steels. LME cracking occurs when molten zinc penetrates prior austenite grain boundaries of the steel substrate. The precise role of silicon in the LME cracking behavior in TRIP and GEN3 steels is unknown. Therefore, a study was undertaken to examine the role of silicon in LME cracking behavior of GEN3 steels. The purpose was also to examine if the presence of retained austenite is required for LME cracking to occur. In this study, laboratory heats were prepared using three silicon levels. Samples cut from galvanized panels were welded using a resistance spot welding machine, and weld areas were examined metallographically for the presence of LME cracks. Gleeble® simulations were done to study the LME behavior of the three steels prepared. Base materials were examined with a scanning electron microscope using the electron back-scattered diffraction (EBSD) method to examine the nature of grain boundaries found. The effect of retained austenite in LME cracking was studied using the Gleeble®. Both RSW and Gleeble® results showed silicon promotes LME cracking in steels, predominantly in the weld heat-affected zones(HAZs). More low-energy, low-coincidence site lattice (CSL) boundaries were found as the silicon content of the steel was decreased. These boundaries do not host cracks. Higher silicon appeared to shrink the safe temperature range over which LME cracks could be avoided, thus indicating heat in-put control to limit cracks has limited windows as the silicon in steel goes up. It was shown that the presence of retained austenite in steel is not a prerequisite for LME cracking to occur.

Critical LME elongation: a criterion measured with Gleeble correlated to LME sensitivity during spot welding

Investigation of the LME Susceptibility of Dual Phase Steel with Different Zinc Coatings

Uncovering the mechanism of the LME susceptibility for the galvanized and electrogalvanized DP 1180 steels

Evaluation of liquid metal embrittlement-free weld by micro-plasma arc welding of Zn-coated interstitial free steel

Liquid Metal Embrittlement Cracking During Resistance Spot Welding of Galvanized Q&P980 Steel

Liquid metal embrittlement and deformation induced martensite: The case of 316 L austenitic steel LME by liquid eutectic gallium-indium

Towards an Explanation of Liquid Metal Embrittlement Cracking in Resistance Spot Welding of Dissimilar Steels

Formation mechanism of liquid metal embrittlement in laser lap welding of zinc-coated GEN3 steels

Comparative Study on the Liquid Metal Embrittlement Susceptibility of the High-Si Advanced High-Strength Steel with EG and GA Zn Coatings

Occurrence of sub-critical heat affected zone liquid metal embrittlement in joining of advanced high strength steel

Liquid metal embrittlement of 12Cr ferritic/martensitic steel thin-walled tubes exposed to liquid lead-bismuth eutectic

The Influence of Electrode Indentation Rate on LME Formation during RSW

Investigation of liquid metal embrittlement of dual phase steel joints by electro-thermomechanical spot-welding simulation

Reducing Liquid Metal Embrittlement Cracking in Resistance Spot Welding of Q&P980 Steel

Zn-induced Liquid Metal Embrittlement and Mechanical Properties of Advanced High-Strength Steel with Resistance Spot Weld

Liquid Metal Embrittlement Susceptibility of the Transformation‐Induced Plasticity Steel/Lead–Bismuth Eutectic System

Liquid Metal Embrittlement Of Galvanized Steel And Its Performance During Resistance Spot Welding

Optimization of hot forming temperature to minimize liquid metal embrittlement induced cracking in resistance spot welded zinc‐coated medium manganese steel

Effect of Silicon and Retained Austenite on the Liquid Metal Embrittlement Cracking Behavior of GEN3 and High-Strength Automotive Steels

Strain-rate controlled Gleeble experiments to determine the stress-strain behavior of HSLA steel S960QL

Temperature-dependent liquid metal embrittlement of Al 0.7 CoCrFeNi high-entropy alloys induced by equiatomic GaInSnZn melts