Properties of polydimethylsiloxane hydrophobic modified duplex microarc oxidation/diamond-like carbon coatings on AZ31B Mg alloy

Xue-Jun Cui,Chuang-Ming Ning,Guang-An Zhang,Lun-Lin Shang,Li-Ping Zhong,Ying-Jun Zhang
DOI: https://doi.org/10.1016/j.jma.2020.04.009
IF: 11.813
2020-10-01
Journal of Magnesium and Alloys
Abstract:A reliable, high-performance coating procedure was developed using PDMS to modify a duplex MAO/DLC coating on an AZ31B Mg alloy. First, the duplex MAO/DLC coating was fabricated via a combined MAO and unbalanced magnetron sputter process. Subsequently, a PDMS solution was used to modify the MAO/DLC coating via a conventional dip-coating method. The surface characteristics, bond strength, hardness, tribological behaviour, and corrosion resistance of the coated samples were evaluated via SEM, CA, Raman spectroscopy, friction and wear behaviour, polarisation curve, and NSS tests. The PDMS modification reduced the <em>H</em><sub>IT</sub> of MAO/DLC coating from 15.96 to 8.34 GPa; this is ascribed to the penetration of PDMS, which has good rheological properties to form a viscoelastic Si-based organic polymer layer on the MAO/DLC coating. However, the PDMS-modified MAO/DLC coating was denser, hydrophobic, and had higher bond strength compared with MAO- and MAO/DLC-coated samples. Moreover, the PDMS modification reduced the COF and wear rate of the duplex MAO/DLC coating. This indicates that the PDMS improved the tribological behaviour owing to the transferred Si oxide that originated from the Si-O network of the PDMS, as well as the low graphitisation of the DLC layer during sliding. Furthermore, the corrosion current density of the MAO/DLC-coated sample modified by PDMS for 10 min decreased by two order of magnitude compared with that of the MAO/DLC-coated sample but by five orders of magnitude compared with that of the bare substrate. The NSS tests proved that the PDMS layer slowed the corrosion of the Mg alloy under long-term service, enhancing the corrosion protection efficiency. The results are attributed to the high bond strength and lubricant MAO/DLC layer, and the dual role of sealing and hydrophobicity of PDMS. Therefore, PDMS modification is promising for the fabrication of protective materials for Mg alloys that require corrosion and wear resistance.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?
### Problems Addressed by the Paper The paper aims to address the limitations in the application of magnesium alloys (Mg alloys) in the automotive, aerospace, and mechanical engineering fields due to their relatively low corrosion resistance and wear resistance. Specifically, the paper explores how to improve the corrosion resistance and wear resistance of AZ31B magnesium alloy by modifying micro-arc oxidation/diamond-like carbon (MAO/DLC) coatings using polydimethylsiloxane (PDMS). ### Main Research Content 1. **Coating Preparation**: - First, MAO/DLC composite coatings were prepared using micro-arc oxidation (MAO) and unbalanced magnetron sputtering processes. - Then, the MAO/DLC coatings were modified with PDMS solution using a dip-coating method. 2. **Performance Evaluation**: - The surface characteristics, adhesion strength, hardness, friction and wear behavior, and corrosion resistance of the coatings were evaluated. - Techniques such as scanning electron microscopy (SEM), contact angle measurement (CA), and Raman spectroscopy were used to characterize the coatings. 3. **Results Analysis**: - PDMS modification significantly reduced the hardness of the MAO/DLC coating (from 15.96 GPa to 8.34 GPa) but increased the coating's density and hydrophobicity. - The PDMS-modified coating exhibited higher adhesion strength and reduced coefficient of friction (COF) and wear rate. - In terms of corrosion resistance, the corrosion current density of the PDMS-modified MAO/DLC coating was reduced by 2 orders of magnitude compared to the unmodified coating and by 5 orders of magnitude compared to the bare substrate. - Neutral salt spray tests indicated that the PDMS layer could slow down the corrosion of magnesium alloys during long-term service, enhancing the anti-corrosion protection efficiency. ### Conclusion The PDMS-modified MAO/DLC coating shows excellent performance in improving the corrosion resistance and wear resistance of magnesium alloys, making it a promising protective material.