Hydrophobic composite layers for enhancing long-term corrosion resistance of Al alloy micro-arc oxidation coating

Qiufeng Mo,Gemei Qin,Wu Wei,Ziying Zhang,Weizhou Li

DOI: https://doi.org/10.1016/j.surfcoat.2022.128979

IF: 4.865

2022-11-25

Surface and Coatings Technology

Abstract:To enhance the long-term corrosion resistance of the micro-arc oxidation (MAO) coating on Al alloys, sealing and hydrophobic modification of MAO coating were carried out in this study. Firstly, isophorone diisocyanate trimer (IPDI) and γ-mercaptopropyltrimethoxysilane (MPTMS) were selected as assembly molecules to alternately assemble layer by layer on the MAO coating. Then SiO2 nanoparticles and 1H, 1H, 2H, 2H-perfluorodecyltrimethoxysilane (TMS) were introduced to the MPTMS/IPDI layer, and a hydrophobic composite coating (MAO-SiO2-TMS) was obtained. The MPTMS/IPDI layer reduced the surface defects and surface roughness and improved the corrosion resistance of the MAO coating. After introducing SiO2 particles and TMS into the MPTMS/IPDI layer, the surface roughness of the coating further decreased from 1.725 μm to 1.1117 μm. The contact angle of the MAO-SiO2-TMS coating reached the superhydrophobic level (150.6°), which was higher than that of the MAO-MPTMS/IPDI (85.3°). In addition, the MAO-SiO2-TMS coating significantly enhanced the long-term corrosion protection of the MAO coating due to the outstanding sealing effect and hydrophobic stability. In particular, the |Z|0.01Hz and Ro of MAO-SiO2-TMS coating were up to 1.71 × 108 Ω·cm2 and 2.56 × 106 Ω·cm2 after 3336 h of exposure to 3.5 % NaCl solution, respectively. The MAO-SiO2-TMS coatings exhibited excellent long-term corrosion resistance in a corrosive environment due to their outstanding sealing effect and hydrophobic stability.

physics, applied,materials science, coatings & films