Corrosion resistance of a superhydrophobic polypropylene coating on magnesium alloy AZ31

Shengjian Zhang,Min Li,Baoyi Li,Hansen Zhao,Feng Wang

DOI: https://doi.org/10.1108/acmm-03-2024-2989

2024-05-19

Anti-Corrosion Methods and Materials

Abstract:Purpose To improve the corrosion resistance of magnesium alloys, the construction of protective coatings is necessary to extend the service life of Mg-based materials. Design/methodology/approach SiO 2 nanoparticles modified by dodecyltrimethoxysilane (DTMS) were added to the PP and a superhydrophobic Mg(OH) 2 /PP-60mSiO 2 composite coating was fabricated on the surface of AZ31 magnesium alloy via the hydrothermal method and subsequently the immersion treatment. Findings Hydrophilic SiO 2 nanoparticles become hydrophobic after modified by DTMS, showing a higher dispersibility in xylene. By incorporating modified SiO 2 nanoparticles into the composite PP coating, the hydrophobicity of the layer was enhanced, resulting in a contact angle of 166.3° and a sliding angle of 3.4°. It also improved the water repellency and durability of the coating. Furthermore, the intermediate layer of Mg(OH) 2 significantly strengthened the bond between the PP layer and the substrate. The Mg(OH) 2 /PP-60mSiO 2 composite coating significantly enhances the corrosion resistance of the magnesium alloy by effectively blocking the infiltration of the corrosion anions during corrosion. The corrosion current density of the Mg(OH) 2 /PP-60mSiO 2 composite coating is approximately 8.23 × 10 –9 A·cm -2 , which can achieve a magnitude three times lower than its substrate, making it a promising surface modification for the Mg alloy. Originality/value The composite coating effectively and durably enhances the corrosion resistance of magnesium alloys.

metallurgy & metallurgical engineering