Abstract:Bimetallic CoCu model catalysts were investigated for the synthesis of higher alcohols using catalytic CO hydrogenation according to the Fischer–Tropsch technology. Emphasis was placed on revealing the influence of the activation conditions. Accordingly, catalyst precursors were activated in argon, hydrogen, syngas (CO/H2), and CO under atmospheric conditions and at elevated temperatures (370 °C). All catalyst precursors were prepared via oxalate coprecipitation in the absence of a classic support. Alcohol selectivities between 30 and ∼40% (up to ∼50% for the sum of alcohols and alkenes) were obtained with an Anderson–Schulz–Flory (ASF) chain lengthening probability maximizing the slate up to C6. Detailed catalysis and characterization studies were performed using a Co2Cu1 catalyst composition. The catalytic performances of the H2- and syngas-activated Co2Cu1 catalyst were similar. While the CO-activated catalyst shows significantly higher catalytic activity and ASF chain lengthening probability, the alcohol selectivities are lower than those of H2- or syngas-activated ones. All catalysts required time on stream for several hours to achieve steady-state catalytic performance. Co2Cu1 catalysts were characterized by temperature-programmed decomposition (TPDec), in situ N2 physisorption (Brunauer–Emmett–Teller), transmission electron microscopy (TEM), and in situ X-ray photoelectron spectroscopy (XPS). The data indicate major restructuring occurs during activation. An “onion-like” graphitic carbon shell was observed via TEM for the CO-activated Co2Cu1 catalyst, which probably originated mainly from the Boudouard reaction (2CO + [ ]ad → Cad + CO2). This interpretation is in accordance with the TPDec profiles and XPS results. The latter also indicates that syngas and CO activation lead to higher than nominal Co/Cu surface ratios. The surface segregation of Co in the presence of CO atmospheres is interpreted on the basis of Co@Cu core–shell structured particles.

Elucidation of reaction network of higher alcohol synthesis over modified FT catalysts by probe molecule experiments

Study on in-situ catalytic conversion of alcohols to aromatics and its mechanism

Enhanced Reaction Performances For Light Olefin Production From Butene Through Cofeeding Reaction With Methanol

Direct Conversion of Syngas to Higher Alcohols over Multifunctional Catalyst: The Role of Copper-Based Component and Catalytic Mechanism

Revealing and Regulating the Complex Reaction Mechanism of CO 2 Hydrogenation to Higher Alcohols on Multifunctional Tandem Catalysts

Higher Alcohols through CO Hydrogenation over CoCu Catalysts: Influence of Precursor Activation

Synthesis of mixed higher alcohols over Fe promoted Cu/ZrO2 catalysts by CO hydrogenation

Enhancing Ethanol Coupling to Produce Higher Alcohols by Tuning H 2 Partial Pressure over a Copper-Hydroxyapatite Catalyst

Accelerating C2+ Alcohols Synthesis from Syngas by Simultaneous Optimizations of CO Dissociation and Chain Growth over CuCo Alloy Catalyst

The steady-state kinetics of CO hydrogenation to higher alcohols over a bulk Co-Cu catalyst

Synthesis Of Higher Alcohol Mixtures From Syngas Over Modified Copper Catalysts

The synthesis of higher alcohols from CO2 hydrogenation over Mn-Cu-K modified Fe5C2 and CuZnAlZr tandem catalysts

Higher alcohols synthesis from syngas over P-promoted non-noble metal Cu-based catalyst

Investigation of Al precursor for ethanol synthesis from syngas on Cu-based multifunctional catalyst

Synergy between Active Sites of Ternary CuZnAlOOH Catalysts in CO Hydrogenation to Ethanol and Higher Alcohols

Catalytic oxidation of isoamyl alcohol on modified ZSM-5 molecular sieve catalysts prepared by different methods

Insight into the structural sensitivity of CuZnAl catalysts for CO hydrogenation to alcohols

Theoretical investigation of the selectivity of alcohols and aldehydes on Co-based catalysts in syngas conversion