Behaviour of painted mirrors during exposure tests to salt spray

E Schütz,F Berger,R Barillon,P Audebert,A Chambaudet

DOI: https://doi.org/10.1016/s0169-4332(97)00219-5

IF: 6.7

1997-11-01

Applied Surface Science

Abstract:The multilayer structure of commercially made mirrors can be subject to degradation under normal conditions, leading to alterations of the mirror's reflective properties. A protective coat of paint, containing an anticorrosive compound, is applied to the copper surface to reduce the oxidation of the thin metallic films. The objective of this study is to analyse the behaviour of the multilayer stack during salt spray tests (neutral salt spray and CASS-test). We followed the morphological and chemical evolution of the interfacial area (glass–silver–copper–paint) using scanning electron microscopy (SEM), and electron probe for micro analysis (EPMA). Studies of the surface of the coatings were performed with attenuated total reflexion infrared spectroscopy (IRTF-ATR) and SEM-EPMA. The observations revealed that a glass–silver decohesion occurs starting at the edges of the material during the tests. The EPMA analyses of the exposed edges of the mirrors indicated first that concentration of the anticorrosive pigment of the paint (lead-based compound) decreased, especially at the copper–paint interface, and second that the copper in the paint may diffuse to the surface of the coating. Finally, IRTF-ATR spectroscopy and SEM-EPMA analyses of surfaces showed that the CASS-test leads to an acid attack of some pigments and extenders of the paint (particularly CaCO3) and leads to chemical modifications of the binder. These phenomena result in an increase in the porosity and a weakening of the paint film. The results obtained with these surface analytical technics will allow us to propose some degradation mechanisms of painted mirrors during salt spray tests.

chemistry, physical,physics, applied, condensed matter,materials science, coatings & films