Mathematical Simulation of Decarburization with CO2 Injection During RH Refining of Ultra-Low-Carbon Steel
Gujun Chen,Jiang Yang,Yugang Li,Shengping He
DOI: https://doi.org/10.1007/s12540-024-01657-1
IF: 3.451
2024-03-30
Metals and Materials International
Abstract:The iron and steel industry is addicted to the resource utilization of carbon dioxide (CO2) produced by themselves. In this study, a mathematical model, based on tanks-in-series model, is developed to describe Ruhrstahl–Heraeus (RH) decarburization during ultra-low-carbon steel refining process when CO2 is injected as the lift gas, and the CO2 bubble surface, bath surface, droplet surface, and bulk steel are selected as decarburization reaction sites. The variation of vacuum chamber pressure during vacuum pumping process can be calculated directly from the mathematical model, and thus, the influence of variation of vacuum chamber pressure on flow and mixing of molten steel as well as decarburization reaction can be considered. The predicted variations in the vacuum chamber pressure and dissolved C and O contents in the molten steel are consistent with industrial data. Simulation results indicate that, compared with Ar injection, the final dissolved C and O contents are respectively increased from 9 and 367 ppm to 20 and 446 ppm for CO2 injection. Therefore, CO2 can be used to completely replace traditional Ar to meet the requirement of a final dissolved C content in molten steel of less than 20 ppm when the initial dissolved C content is 200 ppm and the initial dissolved O content is greater than or equal to 600 ppm. If lower dissolved C and O contents in the molten steel are required at the end, a switching operation from CO2 to Ar injection at the middle stage of decarburization can be performed.Graphical Abstract
materials science, multidisciplinary,metallurgy & metallurgical engineering