Standing 1D Chains Enable Efficient Wide‐Bandgap Selenium Solar Cells

Qingxiang Liu,Xia Wang,Zongbao Li,Wenbo Lu,Xin Wen,Xioayan An,Mingjie Feng,Hui‐Juan Yan,Jin‐Song Hu,Ding‐Jiang Xue

DOI: https://doi.org/10.1002/adma.202410835

IF: 29.4

2024-11-08

Advanced Materials

Abstract:A substrate‐heating strategy is adopted to facilitate the interfacial bonding between Se and substrate, enabling the growth of Se films with a vertical orientation. The resulting Se films exhibit a 4‐times increase in carrier mobility compared to horizontally‐oriented Se films. Solar cells fabricated using these Se films achieve a record efficiency of 8.1%. The recent surge in tandem solar cells and indoor photovoltaics has renewed interest in selenium (Se), the world's first photovoltaic material, due to its intrinsic wide bandgap of ≈1.9 eV, high stability, and non‐toxicity in small quantities when applied in photovoltaics. However, with a 1D chained crystal structure, Se tends to grow crystalline films with a lying orientation—chains parallel to substrates arising from the low surface energy; this results in poor carrier transport across chains held together by weak van der Waals forces. Here a substrate‐heating strategy that facilitates the interfacial bonding between Se and substrate is introduced, enabling the growth of Se films with a standing orientation—chains perpendicular to substrates. This achieves efficient carrier transport along covalently bonded chains. The resulting Se films thereby exhibit a fourfold increase in carrier mobility compared to lying‐oriented Se films. Consequently, Se solar cells are achieved with the highest power conversion efficiency of 8.1% under AM1.5G 1‐sun illumination. The unencapsulated devices exhibit negligible efficiency loss after 1 000 h of storage under ambient conditions.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology