Preserving the stoichiometry

Giulia Tregnago

DOI: https://doi.org/10.1038/s41560-024-01547-1

IF: 56.7

2024-05-29

Nature Energy

Abstract:Solar cells based on kesterites, Cu 2 ZnSn(S x Se 1− x ) 4 (CZTSSe), have recently seen improvement in their power conversion efficiency up to 13.8%. The value is, however, still far from the theoretical efficiency limit of around 33% owing to large voltage losses. These losses are primarily caused by secondary phases and defects forming during the annealing of the material in a selenium-rich atmosphere — a process needed to turn the precursors into a polycrystalline kesterite film. Secondary phases and defects are generally believed to be the result of an alteration of the elemental ratio in the kesterite film driven by loss of tin. Now, Guanglei Cui, Shuping Pang, Zhipeng Shao and team across China suggest that the unbalanced stoichiometry is instead due to the diffusion of copper to the bottom contact layer and that its suppression reduces the formation of defects and ultimately of voltage losses. By means of elemental analysis, the research team show that the diffusion of copper to the molybdenum back contact is inhibited upon the insertion of a 1-nm-thick aluminium oxide blocking layer. The layer is sufficiently thin to suppress copper diffusion while ensuring effective charge transport. The solar cell with the blocking layer shows a homogenous distribution of elements and the concentration of bulk and interfacial defects are reduced by approximately an order of magnitude. The researchers also observe a decrease in the presence of secondary phases. They report an improvement in the open-circuit voltage of the solar cells, achieving a certified power conversion efficiency of 14.6%. The work helps elucidate the factors leading to the formation of secondary phases and defects in kesterite solar cells, providing directions for improving the device performance.

materials science, multidisciplinary,energy & fuels