Enhancement of vanadium addition on hydrogen storage properties of high entropy alloys TiZrFeMnCrV x
Jinting Chen,Haixiang Huang,Tingting Xu,Yujie Lv,Bogu Liu,Bao Zhang,Jianguang Yuan,Ying Wu
DOI: https://doi.org/10.1016/j.ijhydene.2023.09.121
IF: 7.2
2023-09-28
International Journal of Hydrogen Energy
Abstract:High Entropy Alloys (HEAs) have attracted increasing attention due to their unique characteristics, of which the lattice distortion property is particularly beneficial for hydrogen storage. Herein, we prepared the TiZrFeMnCrV HEAs with different V contents and elucidated the effect of V on the hydrogen storage properties. The TiZrFeMnCrV x ( x = 0.5, 1.0, 1.5, 2.0 at%) alloys rapidly absorb 90% of their hydrogen storage capacity within 76 s at 30 °C. Among the alloys, all the three alloys TiZrFeMnCrV x ( x = 1.0, 1.5, 2.0 at%) exhibit higher hydrogen absorption properties, which absorb 1.91, 1.93 and 1.91 wt% of hydrogen at 30 °C, respectively. Among them, the TiZrFeMnCrV x ( x = 1.0 at%) alloy shows the best dehydrogenation performance, starting to release hydrogen at 151.33 °C and terminating at 346.36 °C. Meanwhile, the TiZrFeMnCrV x ( x = 1.0 at%) exhibits remarkable cycle stability and displays a reversible gravimetric capacity of 98% after 15 cycles.
energy & fuels,electrochemistry,chemistry, physical