Unveiling the mechanistic insights into the potassium resistance of 3.5 W-V-1 %K NH 3 -SCR catalysts: The dual functionality of V-O-W structure as acid and redox sites

Xin Yu,Siyuan Xu,Huimin Wang,Rongbing Nie,Junjie Wen,Mengzhao Zhao,Jinyan Cao,Jianjun Chen,Qiulin Zhang,Ping Ning
DOI: https://doi.org/10.1016/j.seppur.2024.129192
IF: 8.6
2024-08-23
Separation and Purification Technology
Abstract:The poisoning effect of alkali metals over Vanadium-based catalysts still faced a significant challenge in the selective catalytic reduction of NOx with NH 3 (NH 3 -SCR). In order to improve the alkali (mainly potassium resistance) resistance of the Vanadium-based catalysts, WO 3 was introduced into the vanadium oxide catalysts. The obtained 3.5WO 3 -V 2 O 5 (3.5 W-V) catalyst exhibited the excellent low-temperature NH 3 -SCR performance owing to the formation of V-O-W structures. Noteworthily, when 1 wt% K was introduced into the 3.5 W-V catalyst, vanadium oxide (V-O, V=O) species preferentially bonded to alkali metal K as an acidic sacrifice site, prompting more active V-O-W species to remain. Thus, the 3.5 W-V catalyst also possessed excellent alkali resistance. The NH 3 -TPD results showed that the 3.5 W-V-1 %K catalyst had a considerable acid site to ensure the adsorption capacity of NH 3 , while the XPS results showed that the 3.5 W-V-1 %K catalyst had excellent redox performance to ensure the activation capacity of the reactant NH 3 . Moreover, in-situ DRIFTS transient experiments revealed that the 3.5 W-V and 3.5 W-V-1 %K catalysts were more capable of adsorbing and activating NH 3 species to rapidly react with gaseous NO, obeying the Eley-Rideal (E-R) pathway in NH 3 -SCR reaction. This work provides new insights into poisoning resistant of vanadium-based catalysts.
engineering, chemical
What problem does this paper attempt to address?