Abstract:The alkali metal poisoned CuNbTi and VWTi catalysts were prepared by wetness impregnation method. Poisoning effects of various K2O mass ratios (0.1%-2%) on CuNbTi and VWTi catalysts were studied, respectively. CuNbTi exhibited an excellent alkali metal resistance that 2%K2O-CuNbTi still remained 80% NOx conversion efficiency and 98% N-2 selectivity while 2%K2O-VWTi was completely deactivated. Moreover, different alkali metals (K, Na, Ca, Mg) with the same molar ratio were doped on CuNbTi. The poisoned degree followed the order: K2O > Na2O > CaO > MgO. Then 2%K2O-CuNbTi and 2%K2O-VWTi were selected for follow-up study. To understand the poisoning mechanism, further investigations were performed by SEM, XRD, N-2-physisorption, XPS, EPR, NH3-TPD, Py-IR, H-2-TPR, in situ DRIFTS characterizations and DFT calculations. The particle of CuNbTi and VWTi agglomerated and the surface area decreased after 2%K2O loading. Loss of acid sites and drop of reducibility resulted in the deactivation of 2%K2O-VWTi. By contrast, experimental and computational results indicated that the alkali resistance of 2%K2O-CuNbTi was mainly due to the interaction between Ti2NbOx support and K atoms that K atoms were preferentially bound to Nb OH and Nb=O with a lower bonding energy of -2.33 eV- -2.83 eV when Cu atoms were coordinated to Ti=O with a binding energy of -1.54 eV. This protected the active copper species from linking to K2O and the weak acid sites were preserved with the increasing isolated Cu2+. Ti2NbOx weakened the impact of potassium on NH3 adsorbing over the catalyst while the preserved copper species provided adsorption sites and redox ability for NH3-SCR reaction. Hence, the synergetic effect of copper and niobium species contributed to the alkali metal resistance. Ti2NbOx trapped the potassium and retained active copper species over 2%K2O-CuNbTi catalyst while potassium deactivated both TiO2 and active vanadium species on 2%K2O-VWTi catalyst. Meanwhile, both Eley-Rideal (E-R) and Langmuir-Hinshelwood (H-L) mechanisms with adsorbed NH3 coordinated to the Lewis acid sites and bidentate nitrate as the dominating intermediate species existed during the NH3-SCR reaction procedure over 2%K2O-CuNbTi at 225 degrees C.

The Poisoning Effect of Alkali Metals Doping over Nano V2O5–WO3/TiO2 Catalysts on Selective Catalytic Reduction of NOx by NH3

The Poisoning Effect of Na+ and Ca2+ Ions Doped on the V2O5/TiO2 Catalysts for Selective Catalytic Reduction of NO by NH3

The Poisoning Effects of Calcium on V2O5-WO3/TiO2 Catalyst for the SCR Reaction: Comparison of Different Forms of Calcium

The Alkali Resistance of CuNbTi Catalyst for Selective Reduction of NO by NH3: A Comparative Investigation with VWTi Catalyst

Alkali Metal Poisoning of A Ceo2-Wo3 Catalyst Used in the Selective Catalytic Reduction of Nox with Nh3: an Experimental and Theoretical Study

Poisoning Effects of Alkali and Alkaline Earth Metal Doping on Selective Catalytic Reduction of NO with NH3 over the Nb-Ce/Zr-PILC Catalysts

The Reaction of Poisonous Alkali Oxides with Vanadia SCR Catalyst and the Afterward Influence: A DFT and Experimental Study

Effects of Potassium, Sodium and Calcium on De-Nox Performance over V2O5/TiO2 Catalysts

The Influence of Alkali Metals on the Ce‐Ti Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx

Potassium Poisoning of Titania Supported Denox Catalysts: Preservation of Vanadia and Sacrifice of Tungsten Oxide

Unraveling Alkali-Tolerance Role of Zeolite Coupling CeWOx Catalyst for NOx Reduction

Effect of Various Acid Anions on Potassium Poisoning and the Mechanism of Commercial V 2 O 5 –WO 3 /TiO 2 Catalysts for SCR of NO x

Unveiling the mechanistic insights into the potassium resistance of 3.5 W-V-1 %K NH 3 -SCR catalysts: The dual functionality of V-O-W structure as acid and redox sites

Like Cures like: Detoxification Effect between Alkali Metals and Sulfur over the V 2 O 5 /TiO 2 deNO x Catalyst

Effects of different introduction methods of Ce4+ and Zr4+ on denitration performance and anti-K poisoning performance of V2O5-WO3/TiO2 catalyst

Alkali Metal Poisoning and Regeneration of Selective Catalytic Reduction Denitration Catalysts: Recent Advances and Future Perspectives

Regeneration of Alkali Poisoned TiO2-based Catalyst by Various Acids in NO Selective Catalytic Reduction with NH3

Unveiling the Mechanistic Insights into the Potassium Resistance of 3.5 W-V-1 %K NH3-SCR 3-SCR Catalysts: the Dual Functionality of V-O-W Structure As Acid and Redox Sites

Inhibition effects of Pb species on the V2O5-MoO3/TiO2 catalyst for selective catalytic reduction of NO with NH3: A DFT supported experimental study

Promotional effect of phosphorus modification on improving the Na resistance of V2O5-MoO3/TiO2 catalyst for selective catalytic reduction of NO by NH3

Support promotion effect on the SO2 and K+ co-poisoning resistance of MnO2/TiO2 for NH3-SCR of NO