Abstract:TiO2-ZrO2 (Ti-Zr) carrier was prepared by a co-precipitation method and 1 wt. % V2O5 and 0.2 CeO2 (the Mole ratio of Ce to Ti-Zr) was impregnated to obtain the V2O5-CeO2/TiO2-ZrO2 catalyst for the selective catalytic reduction of NOx by NH3. The transient activity tests and the in situ DRIFTS (diffuse reflectance infrared Fourier transform spectroscopy) analyses were employed to explore the NH3-SCR (selective catalytic reduction) mechanism systematically, and by designing various conditions of single or mixing feeding gas and pre-treatment ways, a possible pathway of NOx reduction was proposed. It was found that NH3 exhibited a competitive advantage over NO in its adsorption on the catalyst surface, and could form an active intermediate substance of -NH2. More acid sites and intermediate reaction species (-NH2), at lower temperatures, significantly promoted the SCR activity of the V2O5-0.2CeO2/TiO2-ZrO2 catalyst. The presence of O2 could promote the conversion of NO to NO2, while NO2 was easier to reduce. The co-existence of NH3 and O2 resulted in the NH3 adsorption strength being lower, as compared to tests without O2, since O2 could occupy a part of the active site. Due to CeO2’s excellent oxygen storage-release capacity, NH3 adsorption was weakened, in comparison to the 1 wt. % V2O5-0.2CeO2/TiO2-ZrO2 catalyst. If NOx were to be pre-adsorbed in the catalyst, the formation of nitrate and nitro species would be difficult to desorb, which would greatly hinder the SCR reaction. All the findings concluded that NH3-SCR worked mainly through the Eley-Rideal (E-R) mechanism.

New Insights into the Role of WO3 in Improved Activity and Ammonium Bisulfate Resistance for NO Reduction with NH3 over V–W/Ce/Ti Catalyst

Enhanced activity of tungsten modified CeO2/TiO2 for selective catalytic reduction of NOx with ammonia

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Effect of Synthesis Methods on Activity of V2O5/CeO2/WO3-TiO2 Catalyst for Selective Catalytic Reduction of NOx with NH3

New insights into the promotional mechanism of ceria for activity and ammonium bisulfate resistance over V/WTi catalyst for selective catalytic reduction of NO with NH 3

Catalytic Performance of Highly Dispersed WO3 Loaded on CeO2 in the Selective Catalytic Reduction of NO by NH3

Low-temperature Activity and Mechanism of WO3-modified CeO2-TiO2 Catalyst under NH3-NO/NO2 SCR Conditions

V2O5-WO3/TiO2 Catalysts for Low Temperature NH3 SCR: Catalytic Activity and Characterization

Activity Enhancement of Wo3 Modified Fe2o3 Catalyst for the Selective Catalytic Reduction of Nox by Nh3

Effects of WO3 and SiO2 Doping on CeO2–TiO2 Catalysts for Selective Catalytic Reduction of NO with Ammonia

Insight into the role of WO3 on catalytic performance over CuO-CeO2 catalyst for NH3 selective catalytic oxidation reaction

CeO2-WO3 catalysts for the selective catalytic reduction of NOx with NH3: effect of the amount of WO3

Effects of WOx Modification on the Activity, Adsorption and Redox Properties of CeO2 Catalyst for NOx Reduction with Ammonia

Activity enhancement of WO3 modified FeTiO catalysts for the selective catalytic reduction of NO by NH3

NH3-SCR Performance of WO3 Blanketed CeO2 with Different Morphology: Balance of Surface Reducibility and Acidity

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

Excellent low-temperature NH3-SCR of NO activity and resistance to H2O and SO2 over WaCeOx (a=0.06, 0.12, 0.18, 0.24) catalysts: Key role of acidity derived from tungsten addition

Synergistic Effect Between Ceria and Tungsten Oxide on WO3–CeO2–TiO2 Catalysts for NH3-SCR Reaction

V<sub>2</sub>O<sub>5</sub>-WO<sub>3</sub>/TiO<sub>2</sub> Catalysts for Low Temperature NH<sub>3</sub> SCR: Catalytic Activity and Characterization

Promotion Effect of Tungsten Oxide on SCR of NO with NH3 for the V2O5–WO3/Ti0.5Sn0.5O2 Catalyst: Experiments Combined with DFT Calculations

Ultra Hydrothermal Stability of CeO2-WO3/TiO2 for NH3-SCR of NO Compared to Traditional V2O5-WO3/TiO2 Catalyst