Abstract:Vanadia-based catalysts have been widely used for catalyzing various reactions, including their long-standing application in the deNOx process. It has been commonly considered that various vanadium species dispersed on supports with a large surface area act as the catalytically active sites. However, the role of crystalline V2O5 in selective catalytic reduction of NOx with NH3 (NH3-SCR) remains unclear. In this study, a catalyst with low vanadia loading was synthesized, in which crystalline V2O5 was deposited on a TiO2 support that had been pretreated at a high temperature. Surprisingly, the catalyst, which had a large amount of crystalline V2O5, showed excellent low-temperature NH3-SCR activity. For the first time, crystalline V2O5 on low-vanadium-loading catalysts was found to be transformed to polymeric vanadyl species by the adsorption of NH3. The generated active polymeric vanadyl species played a crucial role in NH3-SCR, leading to remarkably enhanced catalytic performance at low temperatures. This new finding provides a fundamental understanding of the metal oxide-catalyzed chemical reaction and has important implications for the development and commercial applications of NH3-SCR catalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/jacs.1c05354?goto=supporting-info">https://pubs.acs.org/doi/10.1021/jacs.1c05354</a>.XRD profiles, NH3-SCR activity, effect of SO2 on NOx conversion, NH3-TPD results, in situ DRIFTS, in situ Raman spectra, DFT calculation, and plot of the change in integral area of various Raman peaks (<a class="ext-link" href="/doi/suppl/10.1021/jacs.1c05354/suppl_file/ja1c05354_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Design of Bifunctional TiO2-SSZ-13 Mixed Supports for Potassium-Resistant Vanadia Catalysts for NH3-SCR

Unveiling the mechanistic insights into the potassium resistance of 3.5 W-V-1 %K NH 3 -SCR catalysts: The dual functionality of V-O-W structure as acid and redox sites

Unveiling the Mechanistic Insights into the Potassium Resistance of 3.5 W-V-1 %K NH3-SCR 3-SCR Catalysts: the Dual Functionality of V-O-W Structure As Acid and Redox Sites

Interface sites on vanadia-based catalysts are highly active for NOx removal under realistic conditions

New Insight into Alkali Resistance and Low Temperature Activation on Vanadia-Titania Catalysts for Selective Catalytic Reduction of NO

Potassium Poisoning of Titania Supported Denox Catalysts: Preservation of Vanadia and Sacrifice of Tungsten Oxide

Cu-SSZ-13 zeolite–metal oxide hybrid catalysts with enhanced SO2-tolerance in the NH3-SCR of NOx

In Situ DRIFTS Studies of NH3-SCR Mechanism over V2O5-CeO2/TiO2-ZrO2 Catalysts for Selective Catalytic Reduction of NOx

Vanadium Substitution As an Effective Way to Enhance the Redox Ability of Tungstophosphoric Acid and for Application of NH3-SCR

Dynamic Change of Active Sites of Supported Vanadia Catalysts for Selective Catalytic Reduction of Nitrogen Oxides

Adsorption-Induced Active Vanadium Species Facilitate Excellent Performance in Low-Temperature Catalytic NO x Abatement

The Reaction of Poisonous Alkali Oxides with Vanadia SCR Catalyst and the Afterward Influence: A DFT and Experimental Study

Ti3+ doped V2O5/TiO2 catalyst for efficient selective catalytic reduction of NOx with NH3

Nh3 Selective Catalytic Reduction of No: A Large Surface Tio2 Support and Its Promotion of V2o5 Dispersion on the Prepared Catalyst

Ammonium Ion Enhanced V2O5-WO3/TiO2 Catalysts for Selective Catalytic Reduction with Ammonia

Active Vanadium(IV) Species Synthesized at Low-Temperature Facilitate Excellent Performance in Low-Temperature NOx-Catalytic Removal

Rational Design of Alkali‐Resistant NO Reduction Catalysts Using a Stable Hexagonal V‐Doped MoO3 Support for Alkali Trapping

Tailoring valence state of V in V-Mo atomically dispersed ensemble enables exceptional NH4HSO4 poisoning resistance for NH3-SCR reaction

Recent Progress on Improving Low-Temperature Activity of Vanadia-Based Catalysts for the Selective Catalytic Reduction of NOx with Ammonia

Sn-doped Rutile TiO2 for Vanadyl Catalysts: Improvements on Activity and Stability in SCR Reaction

Anti-Poisoning Mechanisms of Sb on Vanadia-Based Catalysts for NOx and Chlorobenzene Multi-Pollutant Control