Boosting low-temperature selective catalytic reduction of NO with NH3 of V2O5/TiO2 catalyst via B-doping
Hanghang Li,Wei Zhao,Licheng Wu,Qian Wang,Danhong Shang,Qin Zhong,Hanghang Li,Wei Zhao,Licheng Wu,Qian Wang,Danhong Shang,Qin Zhong
DOI: https://doi.org/10.1016/j.cjche.2021.04.021
IF: 3.8
2022-04-01
Chinese Journal of Chemical Engineering
Abstract:A series of B-doped V2O5/TiO2 catalysts has been prepared the by sol-gel and impregnation methods to investigate the influence of B-doping on the selective catalytic reduction (SCR) of NO x with NH3. X-ray diffraction, Brunauer-Emmett-Teller specific surface area, scanning electron microscope, X-ray photoelectron spectroscopy, temperature-programmed reduction of H2 and temperature-programmed desorption of NH3 technology were used to study the effect of the B-doping on the structure and NH3-SCR activity of V2O5/TiO2 catalysts. The experimental results demonstrated that the introduction of B not only improved the low-temperature SCR activity of the catalysts, but also broadened the activity temperature window. The best SCR activity in the entire test temperature range is obtained for VTiB2.0 with 2.0% doping amount of B and the NO x conversion rate is up to 94.3% at 210 °C. The crystal phase, specific surface area, valence state reducibility and surface acidity of the active components for the as-prepared catalysts are significantly affected by the B-doping, resulting in an improved NH3-SCR performance. These results suggest that the V2O5/TiO2 catalysts with an appropriate B content afford good candidates for SCR in the low temperature window.
engineering, chemical