Abstract:The diminutive additions of nickel (Ni) element have been fused to Sn-1.5Ag-0.5 mass% Cu (SAC155) lead-free solder alloy. The study was examined experimentally and computationally (using JMatPro software program) the microstructural features, thermal behavior, density, thermal diffusivity, and conductivity as well as tensile stress strain of the Sn-1.5Ag-0.5Cu-x mass %Ni (x = 0.00, 0.05, 0.10, 0.20, and 0.50) solder alloys (SAC155-xNi). The fusing additions of Ni have a little impact on the melting point of SAC155 alloy which increasing from 502 to . The microstructure of SAC155 solder alloy included coarse grains of β-Sn besides, large eutectic regions, and embedded IMCs of Ag 3 Sn and Cu 6 Sn 5 . The computed values of Gibbs free energy (G) during solidification of the β-Sn phase, Ag 3 Sn, and Sn 3 Sn 4 IMCs show the stability at , , and , respectively. The SAC155-xNi alloys involved finer β-Sn grains, large fibrous eutectic regions, (Cu,Ni) 6 Sn 5 and (Cu,Ni) 3 Sn 4 IMCs. The G of Cu 6 Sn 5 decreased from to when Ni content increased up to 0.25 mass %, then stable and steady at with more addition of Ni element. The formation of the (Cu, Ni) 6 Sn 5 and (Ni, Cu) 3 Sn 4 IMCs is motivated by the lowest Gibbs free energy, especially when Ni mass% is added to a sufficient level. The measured and computed values of specific heat at constant pressure ( C p ) of SAC155-xNi alloys show a good matching especially at lower temperatures and a little mismatch at high temperatures which decreases with increasing Ni content. The activation energy of atomic arrangement (Q) increased from 11.36 to with increasing Ni content in SAC155-xNi alloys. Thermal diffusivity (α) and conductivity (κ) of SAC155-xNi gradually decreased with increasing temperature in the range from 303 to 423 K and/or Ni content in alloys. The measured values of (κ) are slightly lower than the computed value at similar temperatures of the SAC155-xNi alloys. The decrease in (κ) may be assigned to scattering the electrons or reducing the phonon contributions due to the presence of various solute atoms and different IMCs. The results of stress-strain graphs reveal the enhancement of YS and UTS for all Ni-containing alloys. The improvement of the yield stress (YS) and ultimate tensile strength (UTS) of Ni-containing alloys is attributed to the uniform distribution of the IMCs, the reduction of β-Sn grain size, and the smoothed enlargement of the eutectic region.

Electrical Resistivity of Lead-Free Solders Reinforced by Carbon Nanospheres

Nanocomposite SAC solders: morphology, electrical and mechanical properties of Sn–3.8Ag–0.7Cu solders by adding Co nanoparticles

Wettability and Rheological Behavior of Low Ag Lead-Free SAC/Graphene and Cobalt-Graphene Nanocomposite Solder Paste

Effects of Ni-coated Carbon Nanotubes addition on the electromigration of Sn-Ag-Cu solder joints

Synthesis and analysis of the structure of modified-Al2O3 particles used to increase the strength and electrical conductivity of lead-free solder based on Sn–Ag–Cu

Electrochemical corrosion behaviour of Zn-Sn-Cu-xNi lead-free solder alloys

Shear and Fatigue Properties of Lead-Free Solder Joints: Modeling and Microstructure Analysis

Properties of Sn-Ag-Cu Lead Free Solders with Different Silver Content

Effect of Nano-Al2o3 Reinforcement on the Microstructure and Reliability of Sn–3.0Ag–0.5Cu Solder Joints

Microstructural Examination and Thermodynamic Analysis of Sn-1.5Ag-0.5Cu-x mass% Ni Lead-Free Solder Alloys

Microstructural, thermal and mechanical properties of Co added Sn–0.7Cu lead-free solder alloy

Soldering of Passive Components Using Sn Nanoparticle Reinforced Solder Paste: Influence on Microstructure and Joint Strength

Microstructure and mechanical behavior of Graphene NanoSheets enhanced lead-free Sn–0.3Ag–0.7Cu solder

Effects of Nanoscale Cu 6 Sn 5 Particles Addition on Microstructure and Properties of SnBi Solder Alloys

Effect of Ni-CNTs on Wetting Properties, Microstructure, and Creep Resistance of Sn58Bi-0.1Er Composite Solder

Effect of Ni-CNTs on Microstructure, Thermodynamic Characteristic and Mechanical Properties of Sn58Bi-0.1Er Based Lead-Free Solder

The influences of reactive nanoparticles alloying on grain boundary and melting properties about Sn3.0Ag0.5Cu solder

Microstructural investigations and mechanical properties of pure lead-free (Sn–3.0Ag–0.5Cu and Sn–4.0Ag–0.5Cu) solder alloy

Effects of ZrO2 Nano-Particles' Incorporation into SnAgCu Solder Alloys: An Experimental and Theoretical Study

Effects of Nitrogen on Wettability and Reliability of Lead-Free Solder in Reflow Soldering

Effect of Ni Content on the Microstructure Formation and Properties of Sn-0.7Cu-xNi Solder Alloys