Abstract:Thin-gauge non-oriented silicon steel with high strength was successfully processed using strip casting. Texture evolution and strengthening mechanism via nanoscale Cu-rich precipitates were studied to fundamentally understand the balanced combination of magnetic properties and mechanical properties. Coarse equiaxed grains with average size of ∼190 μm and relatively random texture were formed in the as-cast strip, which contributed to the inhomogeneous deformation, resulting in high density of shear bands. Exact Cube was retained from the initial Cube texture and new Goss was formed during the heavy rolling process in the 0.20 mm cold rolled sheet, which promoted relatively strong Cube and Goss texture after recrystallization annealing. The 0.20 mm annealed sheet exhibited high magnetic induction of 1.709 T, which corresponds to the high texture factor of 0.5. The total iron losses were significantly reduced with decrease in thickness, and the P1.5/50, P1.0/400, and P1.0/1000 in 0.20 mm sheet were as low as 2.63, 15.17 and 55.63 W/kg, respectively, which showed a good match between magnetic induction and iron loss. During the aging process, both the magnetic induction and total iron loss exhibited relatively good stability. With increase in aging time, the yield strength first rapidly increased and then slightly decreased. In 0.20 mm sheet, peak yield strength of ∼630 MPa was obtained on aging at 550 °C for 90–120 min. The key mechanism of precipitation strengthening was attributed to the difference in modulus and coherency strain associated with high density of nanoscale precipitates of ∼5 nm. The study revealed that the nanoscale Cu-rich precipitates can be adopted as effective approach to increase the yield strength over ∼100 MPa without deteriorating iron loss in thin-gauge non-oriented silicon steel by strip casting, which guaranteed the balance of magnetic properties and mechanical properties to meet the requirements of high-speed motor.

The Evolution of Cube Texture in Directionally Solidified Fe-3.0 wt. % Si Alloy Assisted by a High Static Magnetic Field

Evolution of cube texture in strip-cast non-oriented silicon steels

Effect of Electromagnetic Stirring on Fine Grain Formation and Tensile Property Improvement for Fe-Ni Superalloy

Cube Texture Development in Pure Ni during Annealing in a High Strength Magnetic Field

Influence of static magnetic field on rapid solidified structure and nanocrystallization behavior of Fe-Si-B-Cu soft magnetic alloys with pre-existing α-Fe nanocrystals

A comprehensive study on texture evolution and recrystallization mechanism of Fe-4.5 wt% Si with strong {114}

Characterization and Calculation of the Dynamic Recrystallization Texture in Fe-3.0 Wt.% Si Alloy

Effect of process parameters on the texture evolution of Fe-6.5 wt% Si soft magnetic alloys manufactured via laser powder bed fusion

Effects of high static magnetic field on the microstructure of Zn-Bi monotectic alloys during directional solidification process

Crystallization behavior, soft magnetic properties and good bending ductility of high Fe content FeSiBCuPC alloys induced by composition design

A Novel Approach for Evaluating the Influence of Texture Intensities on the First Magnetization Curve and Hysteresis Loss in Fe-Si Alloys

EBSD Study of the Influence of a High Magnetic Field on the Microstructure and Orientation of the Al-Si Eutectic During Directional Solidification

Dislocation Strengthening and Texture Evolution of Non-Oriented Fe-3.3 wt% Si Steel in Double Cold Rolling

Textured, Dense and Giant Magnetostrictive Alloy from Fissile Polycrystal

Effects of Si addition on crystallization process and soft magnetic properties of high-Fe and high-Cu-content Fe-Si-B-P-Cu nanocrystalline alloys

Effect of Dynamic Recrystallization Mode on Texture Components and Hardness for Nano-SiC Particles Reinforced Aluminum Matrix Composites Prepared Via Friction Stir Processing

Thin-gauge non-oriented silicon steel with balanced magnetic and mechanical properties processed by strip casting

Tailoring the microstructure and properties of a Cu–Co immiscible alloy by high magnetic field assisted heat treatment

A unique Fe-based soft magnetic alloy and its magnetic softening mechanism

Formation mechanism of Cube texture components ({001} ) associated with dynamic recrystallization during compression in the single BCC phase region of Ti-22Al-25Nb alloy

Formation Mechanism of Cube Texture Components ({001}<100>) Associated with Dynamic Recrystallization During Compression in the Single BCC Phase Region of Ti-22Al-25Nb Alloy