Abstract:High Performance Polymers, Ahead of Print. Polyimide aerogel, presenting an outstanding new material for lightweight protective thermal insulation, has garnered significant attention in the aerospace field. Despite its potential, due to the high production cost of the supercritical drying method used for its preparation, its widespread application is limited. In this research, a series of lightweight polyimide aerogels (F-PIAs, 3,3',4,4'-biphenyl tetracarboxylic dianhydride (s-BPDA) and 4,4'-diaminodiphenyl ether (ODA)) with excellent thermal protection properties were prepared by lyophilization. The findings indicated that F-PIAs (Freeze-dried polyimide aerogels) exhibited comparable physical characteristics to S-PIAs (Supercritical-dried polyimide aerogels), while their preparation cost was even more economical. F-PIAs exhibits excellent flexible and compression behavior (compression strength up to 1.16 MPa, modulus up to 12.8 MPa), which provide a great structural basis for the production of molded thermal insulation protective materials. The average pore diameter of F-PIAs is in the range of 7∼11 nm. The nanoporous structure leads to the gas within the pores of the aerogel producing the Knudsen effect, thereby significantly enhancing the thermal insulation performance of the aerogel. The thermal conductivity of F-PIA-4 (Freeze-dried polyimide aerogels with a solid content of 4%) at room temperature is as low as 0.023 W·m−1·K−1, which is superior to the PIAs (0.043 W·m−1·K−1) prepared by lyophilization in literature. Its thermal diffusion coefficient changes from 0.108 mm2·s−1 to 0.18 mm2·s−1 in the temperature range of 27°C to 200°C, demonstrating good thermal insulation performance at high temperatures. Meanwhile, after heating on a 150°C flat plate for 11 min and 41 s, the surface temperature of F-PIA-4 was only 36.2°C, further verifying its excellent thermal insulation performance. The results of the TGA experiment on F-PIA-4 demonstrated the high-temperature stability of aerogel (Td5% is higher than 523°C, Td10% is higher than 566°C). The exceptional properties of F-PIAs hold significant practical reference value in helping to reduce the manufacturing cost of high-performance aerogel thermal insulation materials, thereby enabling their widespread application in aerospace, military, and civil field.

Mechanically strong and thermal insulating polyimide/SiO2 aerogel prepared by ambient drying

Synthesis of porous polyimide films with low dielectric constant and excellent mechanical properties by ambient pressure drying

Facile and environment-friendly preparation of high-performance polyimide aerogels using water as the only solvent

Preparation and Characterization of Polyimide Aerogels with a Uniform Nanoporous Framework

Ultrasound-assisted freeze-drying process for polyimide aerogels

Mechanically Strong and Thermally Stable Chemical Cross-Linked Polyimide Aerogels for Thermal Insulator

Transparent, Ultraflexible, and Superinsulating Nanofibrous Biocomposite Aerogels Via Ambient Pressure Drying

Lightweight, Strong, and Super-Thermal Insulating Polyimide Composite Aerogels under High Temperature

Novel atmospheric pressure drying method for silica-based aerogel insulation: Inspired with the adult process of damselflies

Mechanically Robust Nanoporous Polyimide/Silica Aerogels for Thermal Superinsulation of Aircraft

Ultralight and heat-insulating mesoporous polyimide aerogels cross-linked with aminated SiO2 nanoparticles

Konjac glucomannan-based aerogels with excellent thermal stability and flame retardancy for thermal insulation application

Preparation of the methyltriethoxysilane based aerogel monolith with an ultra-low density and excellent mechanical properties by ambient pressure drying

Ultralow shrinkage polyimide hybrid aerogel composite enhanced with organic fibers for thermal protection

Mechanically strong, thermal-insulated, and ultralow dielectric polyimide aerogels with adjustable crosslinking methods

Polyimide aerogels with low thermal conductivity and high-temperature stable properties prepared by lyophilization for flexible thermal protection

Mechanically robust poly(urethane-imide) aerogels with excellent thermal insulation and sound absorption by ambient drying

Enhancing moisture-resistance in polyimide aerogels: A novel hydrophobic modification approach with ortho -positioned long-chain barriers

Facile Synthesis of Flexible and Hydrophobic Polymethylsilsesquioxane Based Silica Aerogel Via the Co-Precursor Method and Ambient Pressure Drying Technique

Mechanically strong and thermally insulating polyimide aerogels by homogeneity reinforcement of electrospun nanofibers

Fumed Silica-Derived, Ambient Dried, and Low-Cost Nanoporous Aerogel-like Monoliths for Thermal Insulation