AlF3-modified anode-electrolyte interface for effective Na dendrites restriction in NASICON-based solid-state electrolyte

Xianguang Miao,Haoxiang Di,Xiaoli Ge,Danyang Zhao,Peng Wang,Rutao Wang,Chengxiang Wang,Longwei Yin

DOI: https://doi.org/10.1016/j.ensm.2020.05.011

IF: 20.4

2020-09-01

Energy Storage Materials

Abstract:<p>Inorganic Na⁺ conducting solid-state electrolyte (SSE) has received extensive attention in assembling large-scale sodium metal batteries. However, continuous Na dendrites propagation has prevailingly hampered its implementation due to premature cell failure and safety concerns. Herein, a coating layer of AlF₃ was decorated between Na anode and NASICON SSE for the first time, which can in situ form a Na⁺ conducting buffer layer by a conversion reaction with Na during initial cycles. Profiting from the intimate modification of AlF₃ interlayer, the Na/SSE interfacial contact is extremely ameliorated. Moreover, owing to the "overpotential triggering" mechanism of the reaction between AlF₃ and Na, the locally agminated electron at the anode-electrolyte interface can be released by preferentially driving more Na⁺ to react with AlF₃ instead of forming dendrites at large current density. According to DFT calculations, the critical dendrites length is also enlarged owing to the increased interfacial energy between AlF₃-induced interlayer and Na. Therefore, the critical current density of Na/AlF₃-NASICON/Na cells has multiplied three-fold to 1.2 mA cm⁻² at60 °C, and the cycling stability of Na metal SSE batteries is also dramatically ameliorated. The rational strategy of modifying AlF₃ interlayer is believed to be helpful in resisting dendrites propagation among solid alkalis metal batteries.</p>

materials science, multidisciplinary,chemistry, physical,nanoscience & nanotechnology