Forging Inspired Processing of Sodium‐Fluorinated Graphene Composite as Dendrite‐Free Anode for Long‐Life Na–CO 2 Cells

Yangjun Mao,Xiao Chen,Hao Cheng,Yunhao Lu,Jian Xie,Tao Zhang,Jian Tu,Xiongwen Xu,Tiejun Zhu,Xinbing Zhao

DOI: https://doi.org/10.1002/eem2.12191

2021-06-28

Abstract:<p>Na‒CO₂ batteries recently are emerging as promising energy-storage devices due to the abundance of Na in the earth's crust and the clean utilization of greenhouse gas CO₂. However, similar to metallic Li, metallic Na also suffers from a serious issue of dendrite growth upon repeated cycling, while a facile method to solve this issue is still lacking. In this work, we report an effective, environmentally friendly method to inhibit Na dendrite growth by in-situ constructing a stable, NaF-rich solid-electrolyte-interface (SEI) layer on metallic Na via adding a small amount (~3 wt%) of fluorinated graphene (FG) in bulk Na. Inspired by the forging processing, a uniform Na/FG composite was obtained by melting and repetitive FG-adsorbing/hammering processes. The Na/FG‒Na/FG half cell exhibits a low voltage hysteresis of 110‒140 mV over 700 h at a current density up to 5 mA cm^–2 with an areal capacity as high as 5 mAh cm^–2. Na‒CO₂ full cell with the Na/FG anode is able to sustain a stable cycling of 391 cycles at a limited capacity of 1000 mAh g^–1. Long cycle life of the cell can be attributed to the protecting effect of the in-situ fabricated NaF-rich SEI layer on metallic Na. Both experiments and density functional theory (DFT) calculations confirm the formation of the NaF-rich SEI layer. The inhibition effect of the NaF-rich SEI layer for Na dendrites is verified by in-situ optical microscopy observations.</p>

materials science, multidisciplinary