Abstract:Neat well cement experience significant strength retrogression at high temperatures above 110 °C, especially at approximately 150 °C. To reveal the mechanism of performance degradation and guide the preparation of high-performance cement, we investigate the hydration process, mechanical behavior, and fracture process for well cement at the temperature of 150 °C based on molecular dynamics simulations and experiments. From triaxial pressure tests and Brazilian splitting tests, the strength, elastic modulus, and Poisson's ratio of well cement decrease drastically with temperature increases from 80 °C to 150 °C. According to XRD, TG/DTG/DSC, and SEM, the hydration degree is insufficient, and larger pores exist in the microstructures. As the main binding phase of well cement, the mechanism of calcium silicate hydrates (C-S-H) influenced by curing temperatures is investigated through molecular dynamics simulations. C-S-H with calcium/silicon ratios (C/S) of 1.1 and 1.8 are simulated in the aqueous and solid states to investigate precipitation and mechanical behaviors. By reducing the C/S ratio to 1.1, the strength rebounds to a certain extent, and the adequacy of the hydration degree improved. It is found from the polymerization process that the increasing temperature promotes the polymerization rate, which is higher with C/S = 1.8 than that of 1.1. However, an increase in the C/S ratio will lead to a decrease in bridging oxygen content, thus a lower polymerization degree. The fracture simulations of C-S-H gels at different temperatures indicate that the failure of the C-S-H structure is mainly attributed to the disassembling of the calcium oxygen layers. With a higher temperature, there are fewer Ca-O bonds breaking, thus less strain energy consumed, resulting in worse performance. The elasticity of C-S-H, including Young's and shear moduli, also exhibits certain degradations at a higher temperature. The elastic behavior of C-S-H with a low C/S ratio is generally higher than the high C/S.

Temperature affected cement foaming and foams

Experimental Study and Molecular Simulation of the Effect of Temperature on the Stability of Surfactant Foam

Fluidizing Effects of Polymers with Various Anchoring Groups in Cement Pastes and Their Sensitivity to Environmental Temperatures

Influencing factors of mechanical and thermal conductivity of foamed phosphogypsum-based composite cementitious materials

Study on the rheological properties of Portland cement pastes with polycarboxylate superplasticizers

Temperature Effect of Hydration and Microstructure of Tricalcium Silicate–Slag Powder Hydrated Composites: An Experimental and Molecular Dynamics Investigation

Effect of Curing Temperature on Mechanical Strength and Thermal Properties of Hydraulic Limestone Powder Concrete

Characterizing the foam-shell microstructure of industrial ultra-light foamed concrete cast under different temperatures

Study on the thermodynamic properties of low density modified foamed cement

Effects of Curing Temperature on Rheological Behaviour and Compressive Strength of Cement Containing GGBFS

Effects of Tuff Powder on the Hydration Properties of Cement-Based Materials under High Temperature

Effect of High Temperature on Compressive Strength and Microstructure of Cement Paste Modified by Micro- and Nano-calcium Carbonate Particles

Influence of Early Hydration Process on the Hydrostatic Pressure Change of Cement Pastes at Different Temperatures

Effect of Elevated Temperature on Mechanical Properties of High-Volume Fly Ash-Based Geopolymer Concrete, Mortar and Paste Cured at Room Temperature

Early-Age Hydration Heat Evolution and Kinetics of Portland Cement Containing Nano-Silica at Different Temperatures

Physio-chemical effects on the temperature-dependent elasticity of cement paste during setting

Effect of Hydration Temperature Rise Inhibitor on the Temperature Rise of Concrete and Its Mechanism

Influence of Curing Temperature on the Performance of Calcined Coal Gangue-Limestone Blended Cements

Insight into Class G Wellbore Cement Hydration and Mechanism at 150 °C Using Molecular Dynamics

Computational modeling and simulation of temperature field evolution during the chemical foaming of epoxy foams

Effect of Temperature on Pore Structure and Strength of Concrete