Abstract:A low-temperature solid oxide fuel cell (LT-SOFC) is a next-generation energy conversion device and has advantages of high energy efficiency, fast start up and shut down and eco-friendliness. In addition, since it has the advantage of being able to use various fuels such as hydrogen, alcohol, and methane gas, research is being actively conducted in recent years. However, LT-SOFC using hydrogen as a fuel has difficulties in storing and transporting fuel, making it difficult to apply as a portable device. On the other hand, methanol fuel is an attractive alternative fuel because it is easier to transport and store than hydrogen fuel and has a high volumetric energy density. However, when methanol is applied to LT-SOFC, there is a disadvantage in performance due to the complicated oxidation process and CO poisoning. Complex methanol oxidation reaction (MOR) and CO poisoning reduce the performance and durability of fuel cells. Therefore, it is important to use a catalyst that can prevent CO poisoning and improve the oxidation reaction of methanol. Pt is an effective catalyst for methanol decomposition and is one of the materials widely used in direct methanol fuel cell (DMFC). However, there is a problem in that it is vulnerable to CO generated during the methanol oxidation process. It is known that CO is adsorbed on the Pt surface, blocks the active site, and reduces catalytic activity. Therefore, alloying Pt with samaria-doped ceria (SDC) with high oxygen storage capacity (OSC) and good OH generation capacity can be effective to reduce CO poisoning and coking. In this study, we prepared the cells with Pt-SDC cermet anodes with the Pt volume percent of 69 (Pt 0.69), 83 (Pt 0.83), 92 (Pt 0.92), and 95 (Pt 0.95) volume% by varying Pt and SDC powers in the co-sputtering process. In the electrochemical impedance spectroscopy (EIS), ohmic resistance was similar between all samples; on the other hand, activation resistance was measured to be 24.0, 19.5, 31.8, 30.8, and 53.0 Ω∙cm 2 at Pt 0.69, Pt 0.83, Pt 0.92, Pt 0.95, and Pt 1 samples, respectively, confirming the lowest activation resistance at Pt 0.83. We speculate that the MOR is improved by the increase of triple phase boundary (TPB) sites and the facilitation of bifunctional CO oxidation mechanisms with higher content of SDC up to 17 mol% (Pt 0.83). However, in the anode with excessive SDC content (31 mol%, Pt 0.69), the Pt is oxidized to form PtO 2 , lowering the catalytic activity.

Direct methanol oxygen-ion conducting solid oxide fuel cell with an integrated in-situ cracking reactor

Direct liquid methanol-fueled solid oxide fuel cell

Durability of Direct Internal Reforming of Methanol As Fuel for Solid Oxide Fuel Cell with Double-Sided Cathodes

Development of Methanol-Fueled Low-Temperature Solid Oxide Fuel Cells

A Robust Fuel Cell Operated on Nearly Dry Methane at 500 °C Enabled by Synergistic Thermal Catalysis and Electrocatalysis

Direct Operation of Solid Oxide Fuel Cells on Low-Concentration Oxygen-Bearing Coal-Bed Methane with High Stability

High-rate Electrochemical Partial Oxidation of Methane in Solid Oxide Fuel Cells

A Robust Flat-Chip Solid Oxide Fuel Cell Coupled with Catalytic Partial Oxidation of Methane

Power Generation from a Symmetric Flat-Tube Solid Oxide Fuel Cell Using Direct Internal Dry-Reforming of Methane

Methanol Fueled Low Temperature Solid Oxide Fuel Cell with Pt-SDC Anodes

Direct power generation from methanol by solid oxide fuel cells with a Cu-ceria based catalyst layer

Low-temperature ceria-electrolyte solid oxide fuel cells for efficient methanol oxidation

Performance of solid-oxide fuel cells operating with different sustainable fuel reformates

Direct Operation of Solid Oxide Fuel Cells with Methane Fuel

Direct-Methane Solid Oxide Fuel Cells with Hierarchically Porous Ni-Based Anode Deposited with Nanocatalyst Layer

Direct Use of Coke in a Solid Oxide Fuel Cell

The Performance of Solid Oxide Fuel Cells Based on Methanol Solution

Controlled Deposition and Utilization of Carbon on Ni-Ysz Anodes of Sofcs Operating on Dry Methane

Ethanol-fueled metal supported solid oxide fuel cells with a high entropy alloy internal reforming catalyst

Degradation mechanisms and mitigation strategies of direct methane solid oxide fuel cells