Microstructure and Mechanical Properties of Bimetallic Materials Containing Ceramic Particles Made Using Directed Energy Deposition

Pengfei Li,Qingtao Yang,Jun Yin,Yuchun Peng,Zhiqiang Zhang,Ruitao Li,Jinzhong Lu

DOI: https://doi.org/10.1007/s11665-024-10338-4

IF: 2.3

2024-10-26

Journal of Materials Engineering and Performance

Abstract:This study employs directed energy deposition to fabricate metal matrix composite (MMC) consisting of 95% IN718 and 5% (75% Cr 2 O 3 + TiO 2 ), as well as SS316, resulting in bimetallic materials. The interface characteristics, microstructural morphology, and hardness distribution under different deposition sequences are studied. Several characterization techniques such as scanning electron microscopy (SEM) and multifunctional x-ray photoelectron spectroscopy (XPS) are utilized to thoroughly investigate the elemental distribution at the interfaces and their oxidation states. The results show that the transition layer width at the MMC/SS316 interface is three times that of the SS316/MMC interface, and the microhardness at the SS316/MMC interface is higher than on either side of the interface. The longitudinal tensile yield strength (595 MPa) is significantly higher than the transverse tensile yield strength (434 MPa). By adjusting the deposition sequence and laser processing parameters, the microstructure and mechanical properties of the bimetallic interface can be effectively controlled, offering new possibilities for applications in fields such as aerospace, automotive manufacturing, and the nuclear industry.

materials science, multidisciplinary